ML35 - GB /T 5953.1-2009

Grade	ML35
Corresponding Standard	GB /T 5953.1-2009 Steel Wire for Cold Heading and Cold Forging— Part 1: Intended for Heat Treatment
Classification	Carbon Steel

ML35 Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S
Minimum Value	0.33	0.1	0.6	-	-
Maximum Value	0.38	0.3	0.9	0.025	0.025

ML35 Mechanical Properties

diameter d mm	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Reduction of Area ψ %	Hardness HBW
d≤6	SALD	490~690	≥55
6＜d≤12	SALD	470~650	≥55
12＜d≤25	SALD	450~600	≥50	HRB ≤89
d≤25	SA	380~560	≥60	HRB ≤86

Approximate Comparison Table Cold Heading Steel

China

Taiwan, China

Japan

South Korea

United States

International Organization for Standardization

Germany

France

Russia

United Kingdom

ISC

CNS

JIS

ASTM/AISI

UNS

ISO

DIN EN/DIN

W-Nr.

NF EN/NF

GOST

BS EN/BS

ML35

U40352

SWRCH35K

1034

G10340

CE35E4
(C3)

Cq35
(C35C)

1.1172

XC38
FR36

1/2

ML35 Corresponding Standards(Same grade name, different standards)

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!