GX5CrNi19-10 1.4308 - EN 10213-2007(+A1:2016)

Grade	GX5CrNi19-10
European Standard Steel Grade	1.4308
Corresponding Standard	EN 10213-2007(+A1:2016) Steel Castings for Pressure Purposes
Classification	Cast Steel

GX5CrNi19-10 Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Ni	Cu
Minimum Value	-	-	-	-	-	18	8	-
Maximum Value	0.07	1.5	1.5	0.04	0.03	20	11	0.5

GX5CrNi19-10 Mechanical Properties

thickness t mm	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Impact Energy Absorption KV2 J
t ≤ 150	Solution Heat Treatment + Water Quenching (AT)①	440~640	Rp1.0：≥200	A: ≥30	Room temperature: ≥60 -196°C: ≥60

1 Approximate Comparison Table Corrosion-Resistant Cast Steels

China

Taiwan, China

Japan

South Korea

United States

Germany

France

Russia

Sweden

United Kingdom

ISC

CNS

JIS

ASTM

UNS

DIN EN/DIN

W-Nr.

NF EN/NF

GOST

SS₁₄

BS EN/BS

ZG07Cr19Ni9

C53048

SCS 13A

SSC 13A

CF8

J92600

GX5CrNi19-10

1.4308

Z2CN18.10M

07Х18Н9Л

2333

304C15

2 Approximate Comparison Table Corrosion-Resistant Cast Steels

China		Taiwan, China	Japan	South Korea	International Organization for Standardization	Germany		France	Russia	Sweden	United Kingdom
GB	ISC	CNS	JIS	KS	ISO	DIN EN/DIN	W-Nr.	NF EN/NF	GOST	SS₁₄	BS EN/BS
ZG07Cr19Ni9	C53048	SCS 13	SCS 13X	SSC 13	GX5CrNi19-9	GX5CrNi19-10	1.4308	Z2CN18.10M	07Х18Н9Л	2333	304C15

GX5CrNi19-10 Corresponding Standards(Same grade name, different standards)