SWRCH15K - H2ABC

Grade	SWRCH15K
Classification	Carbon Steel

SWRCH15K Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S
Minimum Value	0.13	0.1	0.3	-	-
Maximum Value	0.18	0.35	0.6	0.03	0.035

1 Approximate Comparison Table Cold Heading Steel

China

Taiwan, China

Japan

South Korea

United States

International Organization for Standardization

Germany

France

Russia

United Kingdom

ISC

CNS

JIS

ASTM/AISI

UNS

ISO

DIN EN/DIN

W-Nr.

NF EN/NF

GOST

BS EN/BS

ML15

U40152

SWRCH15K

1015

G10150

CC15A
(A4Al)

QSt38-3
(C14C)
Cq15
(C15C)

1.0234
-
1.1132

FR15
FB18
FR18

15пс

0/3

2 Approximate Comparison Table Steel for Cold Heading and Cold Extrusion

China		Japan	United States	International Organization for Standardization	European Standard
GB	ISC	JIS	ASTM	ISO	EN	Numerical Grade
ML15	U40152	SWRCH15K	1015	CC15K	C15C	1.0234

3 Approximate Comparison Table Steel for Cold Heading and Cold Extrusion

China		Japan	United States	International Organization for Standardization	European Standard
YB	GB	JIS	ASTM	ISO	EN
QML15	ML15	SWRCH15K	1015	C15GC	C15E2C

4 Approximate Comparison Table Steel for Cold Heading and Cold Extrusion

China	Japan	United States	International Organization for Standardization	European Standard
GB	JIS	ASTM	ISO	EN
ML15	SWRCH15K	1015	C15GC	C15E2C

5 Approximate Comparison Table Steel for Cold Heading and Cold Extrusion

China	Japan	International Organization for Standardization
GB	JIS	ISO
ML15	SWRCH15K	C15GC