Home Material EN 10263-5-2017
简体 | 繁體
Grade X6CrMo17-1
European Standard Steel Grade 1.4113
Corresponding Standard EN 10263-5-2017
Steel rod, bars and wire for cold heading and cold extrusion - Part 5: Technical delivery conditions for stainless steels
Classification Ferritic Stainless Steel
Properties Corrosion Resistance
Density 7.7 g/cm3
X6CrMo17-1 Chemical Element Composition Content (%)
Component C Si Mn P S ⓑ Cr Mo
Minimum Value - - - - - 16 0.9
Maximum Value 0.08 1 1 0.04 0.03 18 1.4
X6CrMo17-1 Mechanical Properties
condition Heat Treatment or Condition
Tensile Strength
σb
Mpa 		Reduction of Area
ψ
%
Rod, Wire; 2<d≤5 Softening Annealing + Cold Drawn + Softening Annealing (+A+C+A) ≤600 ≥60
Wire; 2<d≤5 Annealing Softening + Cold Drawing + Annealing Softening + Quenching Rolling (+A+C+A+LC) ≤660 ≥58
Bar stock, rod stock, wire; 5 < d ≤ 10 Softening Annealing (+A) or Softening Annealing + Pickling (+A+PE) ≤600 ≥60
Wire; 5<d≤10 Softening Annealing + Quenching + Softening Annealing (+A+LC) ≤710 ≥57
Rod, Wire; 5<d≤10 Softening Annealing + Cold Drawn + Softening Annealing (+A+C+A) ≤600 ≥60
Wire; 5<d≤10 Annealing Softening + Cold Drawing + Annealing Softening + Quenching Rolling (+A+C+A+LC) ≤640 ≥58
Bar stock, rod stock, wire stock; 10 < d ≤ 25 Softening Annealing (+A) or Softening Annealing + Pickling (+A+PE) ≤600 ≥60
Wires; 10<d≤25 Softening Annealing + Quenching + Softening Annealing (+A+LC) ≤690 ≥57
Wires; 10<d≤25 Annealing Softening + Cold Drawing + Annealing Softening + Quenching Rolling (+A+C+A+LC) ≤600 ≥60
1 Approximate Comparison Table
China Taiwan, China Japan South Korea United States International Organization for Standardization Germany France European Standard Sweden United Kingdom
GB ISC CNS JIS KS ASTM/AISI UNS ISO Numerical Grade DIN EN/DIN W-Nr. NF EN/NF EN Numerical Grade SS BS EN/BS
10Cr17Mo
(1Cr17Mo) 		S11790 434 SUS 434 STS 434 434 S43400 X6CrMo 17-1
9c
(ISO 683-13-1986) 		4113-434-00-I X6CrMo 17-1
(X6CrMo 17) 		1.4113
1.4113 		Z8CD 17-01 X6CrMo 17-1 1.4113 2325 434S17
434S19
2 Approximate Comparison Table
China Japan United States International Organization for Standardization Germany Sweden
GB JIS ASTM ISO DIN EN/DIN W-Nr. SS
3Cr17Mo SUS 434 440 X38CrMo16 X6CrMo 17-1 1.4113 2325
3 Approximate Comparison Table Stainless steels for cold heading and cold extruding
China Japan United States International Organization for Standardization European Standard
GB ISC JIS ASTM/AISI UNS ISO Numerical Grade EN Numerical Grade
10Cr17Mo
(1Cr17Mo) 		S11790 SUS434 434 S43400 X6CrMo17-1 4113-434-00-I X6CrMo17-1 1.4113
X6CrMo17-1 Corresponding Standards(Same grade name, different standards)
1 EN 10088-1-2005
X6CrMo 17-1 1.4113
2 EN 10263-5-2001
X6CrMo17-1 1.4113
3 ISO TS 15510-2003
X6CrMo17-1
4 EN 10088-3-2005
X6CrMo17-1 1.4113
5 EN 10088-3-2014
X6CrMo17-1 1.4113
6 ISO 15510-2014
X6CrMo17-1 4113-434-00-I
7 DIN EN 10263-5-2018
X6CrMo17-1 1.4113
8 DIN EN 10088-3-2014
X6CrMo17-1 1.4113
9 ISO 683-18-2014
X6CrMo17-1 4113-434-00-I
10 ISO 4954-2018
X6CrMo17-1 4113-434-00-I
11 NF EN 10088-2-2005
X6CrMo17-1 1.4113
12 NF EN 10088-1-2005
X6CrMo17-1 1.4113
13 EN 10263-5-2017
X6CrMo17-1 1.4113
14 ISO 4954-2-2024
X6CrMo17-1 4113-434-00-I

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!