Grade X6CrNiMoTi 17-12-2
European Standard Steel Grade 1.4571
Corresponding Standard EN 10263-5-2017
Steel rod, bars and wire for cold heading and cold extrusion - Part 5: Technical delivery conditions for stainless steels
Classification Austenitic Stainless Steel
Properties Corrosion Resistance
Density 8 g/cm3
X6CrNiMoTi 17-12-2 Chemical Element Composition Content (%)
Component C Si Mn P S ⓑ Cr Ni Cu Mo More
Minimum Value - - - - - 16.5 10.5 - 2 Ti：5C~0.7
Maximum Value 0.08 1 2 0.045 0.03 18.5 13.5 1 2.5
X6CrNiMoTi 17-12-2 Mechanical Properties
condition Heat Treatment or Condition
Tensile Strength
σb
Mpa 		Reduction of Area
ψ
%
Rod, Wire; 2<d≤5 Solid Solution + Cold Drawing + Solid Solution (+AT+C+AT) ≤720 ≥65
Wire; 2<d≤5 Solid Solution + Cold Drawn + Solid Solution + Quenched Rolling (+AT+C+AT+LC) ≤770 ≥60
Bar, rod, wire; 5<d≤10 Solid Solution (+AT) or Solid Solution + Decap (+AT+PE) ≤680 ≥65
Rod, wire; 5<d≤10 Solid Solution + Cold Drawn (+AT+C) ≤850 -
Rod, Wire; 5<d≤10 Solid Solution + Cold Drawing + Solid Solution (+AT+C+AT) ≤680 ≥65
Wire; 5<d≤10 Solid Solution + Cold Drawn + Solid Solution + Quenched Rolling (+AT+C+AT+LC) ≤730 ≥60
Bar, rod, wire; 10<d≤25 Solid Solution (+AT) or Solid Solution + Decap (+AT+PE) ≤680 ≥65
Rod, wire; 10<d≤25 Solid Solution + Cold Drawn (+AT+C) ≤810 -
Rod, Wire; 10<d≤25 Solid Solution + Cold Drawing + Solid Solution (+AT+C+AT) ≤680 ≥65
Bar, rod, wire; 25<d≤50 Solid Solution (+AT) or Solid Solution + Decap (+AT+PE) ≤680 ≥65
1 Approximate Comparison Table
China Taiwan, China Japan South Korea United States International Organization for Standardization Germany France European Standard Russia Sweden United Kingdom
GB ISC CNS JIS KS ASTM UNS ISO Numerical Grade DIN EN/DIN W-Nr. NF EN/NF EN Numerical Grade GOST SS BS EN/BS
06Cr17Ni12Mo2Ti S31668 316Ti SUS 316Ti STS 316Ti 316Ti S31635 X6CrNiMoTi 17-12-2 4571-316-35-I X6CrNiMoTi 17-12-2
(X10CrNiMoTi 18-10) 		1.4571 Z6CNDT 17-12 X6CrNiMoTi 17-12-2 1.4571 08Х17Н13М2Т 2350 320S31
320S17
2 Approximate Comparison Table
China Japan United States Germany France European Standard Russia Sweden United Kingdom
GB JIS ASTM DIN EN/DIN NF EN/NF EN Numerical Grade GOST SS BS EN/BS
0Cr18Ni12Mo2Ti
1Cr18Ni12Mo2Ti 		316Ti
SUS316Ti 		316Ti X10CrNiMoTi18-10
X6CrNiMoTi17-12-2 		Z6CNDT17-12
Z6CNT17-12 		X6CrNiMoTi17-12-2 1.4571 08KH17N13M2T
10KH17N13M2T 		2350
2350-02 		320S31
321S12
3 Approximate Comparison Table Stainless steels for cold heading and cold extruding
China Japan United States International Organization for Standardization European Standard
GB ISC JIS ASTM/AISI UNS ISO Numerical Grade EN Numerical Grade
06Cr17Ni12Mo2Ti
(0Cr18Ni12Mo3Ti) 		S31668 SUS316Ti 316Ti S31635 X6CrNiMoTi17-12-2 4571-316-35-I X6CrNiMoTi17-12-2 1.4571
X6CrNiMoTi17-12-2 Corresponding Standards(Same grade name, different standards)
1 EN 10088-1-2005
X6CrNiMoTi 17-12-2 1.4571
2 EN 10296-2-2005
X6CrNiMoTi17-12-2 1.4571
3 EN 10253-4-2003
X6CrNiMoTi17-12-2 1.4571
4 EN 10263-5-2001
X6CrNiMoTi17-12-2 1.4571
5 EN 10250-4-1999
X6CrNiMoTi 17-12-2 1.4571
6 ISO TS 15510-2003
X6CrNiMoTi17-12-2
7 EN 10088-2-2005
X6CrNiMoTi17-12-2 1.4571
8 DIN 17440-1972
X6CrNiMoTi 17-12-2 X10CrNiMoTi 18-10 1.4571
9 EN 10088-3-2005
X6CrNiMoTi 17-12-2 1.4571
10 EN 10297(2)-2005
X6CrNiMoTi17-12-2 1.4571
11 EN 10088-3-2014
X6CrNiMoTi 17-12-2 1.4571
12 ISO 15510-2014
X6CrNiMoTi17-12-2 4571-316-35-I
13 DIN EN 10263-5-2018
X6CrNiMoTi 17-12-2 1.4571
14 ISO 9328-7-2018
X6CrNiMoTi17-12-2
15 DIN EN 10088-3-2014
X6CrNiMoTi 17-12-2 1.4571
16 ISO 683-18-2014
X6CrNiMoTi17-12-2 4571-316-35-I
17 ISO 4954-2018
X6CrNiMoTi17-12-2 4571-316-35-I
18 NF EN 10088-2-2005
X6CrNiMoTi17-12-2 1.4571
19 NF EN 10088-1-2005
X6CrNiMoTi17-12-2 1.4571
20 NF EN 10028-7-2008
X6CrNiMoTi17-12-2 1.4571
21 NF EN 10296-2-2005
X6CrNiMoTi17-12-2 1.4571
22 NF EN 10028-7-2000
X6CrNiMoTi17-12-2 1.4571
23 EN 10263-5-2017
X6CrNiMoTi 17-12-2 1.4571
24 ISO 4954-2-2024
X6CrNiMoTi17-12-2 4571-316-35-I
25 DIN EN 10296-2-2006
X6CrNiMoTi17-12-2 1.4571

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!