GH2132 - GJB 3167-1988

Grade	GH2132
Corresponding Standard	GJB 3167-1988 Specification for cold drawn wires of heat-resisting superalloy for cold upsetting
Classification	Special Alloy Steel

GH2132 Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Ni	Mo	Ti	V	B	Al	More
Minimum Value	-	0.4	1	-	-	13.5	24	1	1.75	0.1	0.001	-	Fe:Remainder
Maximum Value	0.08	1	2	0.025	0.02	16	27	1.5	2.35	0.5	0.01	0.4	Fe:Remainder

• B and Ce are added based on calculated amounts and are not analyzed. The addition amounts shall be specified in the quality certificate.
• The permissible deviations in the chemical composition of wire rods shall comply with Table 4 of the original GB/T 14992 standard.
• Upon the buyer\'s request, alloys with stricter composition ranges than those specified in the table can be supplied.

GH2132 Mechanical Properties

condition	Test Temperature	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Reduction of Area ψ %	Hardness HBW
Wire material	Room Temperature	980~1000°C, Water (Oil) Cooling	-		-		HBS10/3000: ≤201(≥4.25) HV: ≤194
sample	Room Temperature	Solution heat treatment + 700~720°C, 16h, air cooling②	≥900	≥580	≥15	≥20	HBS10/3000: 341~248 HV: 260~360
sample	Room Temperature	Solution heat treatment + 700~720°C, 16h, air cooling②	(≥930)	-	(≥18)	(≥40)	HBS10/3000: 341~248 HV: 260~360
sample			Stress 450MPa, fracture time ≥23h③
sample			Stress 392MPa, fracture time (≥100h)③

GH2132 Corresponding Standards(Same grade name, different standards)

1	GB /T 14992-2005
	GH2132 H21320 (GH132)
2	GB /T 14994-2008
	GH2132 H21320 (GH132)
3	GB /T 14995-2010
	GH2132 (GH132)
4	GB /T 14996-2010
	GH2132 (GH132)
5	YB /T 5245-1993
	GH2132 (GH132)
6	GJB 2611A-2006
	GH2132 (GH132)
7	GJB 3167-1988
	GH2132
8	GB /T 40313-2021
	GH2132

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!