GH1140 - GJB 3167-1988

Grade	GH1140
Corresponding Standard	GJB 3167-1988 Specification for cold drawn wires of heat-resisting superalloy for cold upsetting
Classification	Special Alloy Steel

GH1140 Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Ni	Mo	Ti	W	Al	Ce	More
Minimum Value	0.06	-	-	-	-	20	35	2	0.7	1.4	0.2	-	Fe:Remainder；Al+Ti≤1.75
Maximum Value	0.12	0.8	0.7	0.025	0.015	23	40	2.5	1.2	1.8	0.6	0.05	Fe:Remainder；Al+Ti≤1.75

• B and Ce are added based on calculated amounts and are not analyzed. The addition amounts shall be specified in the quality certificate.
• The permissible deviations in the chemical composition of wire rods shall comply with Table 4 of the original GB/T 14992 standard.
• Upon the buyer\'s request, alloys with stricter composition ranges than those specified in the table can be supplied.

GH1140 Mechanical Properties

condition	Test Temperature	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Elongation or Extension Rate δ %	Hardness HBW
Wire material	Room Temperature	1050~1080°C, Air cooling	≤735	≥40	-

GH1140 Corresponding Standards(Same grade name, different standards)

1	GB /T 14992-2005
	GH1140 H11400 (GH140)
2	GB /T 14995-2010
	GH1140 (GH140)
3	GB /T 14996-2010
	GH1140 (GH140)
4	GB /T 15062-2008
	GH1140
5	YB /T 5245-1993
	GH1140
6	GJB 3167-1988
	GH1140