H65 C27000 - GB /T 3114-1994

Grade	H65
China ISC	C27000
Corresponding Standard	GB /T 3114-1994 Copper and Copper Alloy Rectangular Wires
Classification	Copper and Copper Alloys
Properties	Strength

H65 Chemical Element Composition Content (%)

Component	Fe	Cu	Pb	Other Total	More
Minimum Value	-	63	-	-	Zn:余量
Maximum Value	0.07	68.5	0.09	0.45	Zn:余量

"Other individual elements or other totals": The chemical composition includes elements not specified in the table. Analysis should only be conducted if these elements are suspected to be present, or if routine analysis suggests that their content may exceed the prescribed limits.

H65 Mechanical Properties

	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Elongation or Extension Rate δ %
0.5~12	Soft (M)	≥245	≥28
0.5~12	Half Hard (Y2)	≥295	≥12
0.5~12	Hard (Y)	≥440	-

1 Approximate Comparison Table Brass

China	Japan	United States		International Organization for Standardization		Germany		European Standard		Russia
GB	JIS	ASTM	UNS	ISO	Numerical Grade	DIN EN/DIN	W-Nr.	EN	Numerical Grade	GOST
H65	C2700	65Cu-35Zn	C27000	CuZn36	C27000	CuZn36	C27000 2.0335	CuZn36	CW507L	Л65

2 Approximate Comparison Table Brass

China	Japan	United States	International Organization for Standardization	Germany	United Kingdom
GB	JIS	ASTM	ISO	DIN EN/DIN	BS EN/BS
H65	C2700	C27000	CuZn35	CuZn36	CZ107

H65 Corresponding Standards(Same grade name, different standards)

1	GB /T 5231-2012
	H65 C27000
2	GB /T 2040-2017
	H65 C27000
3	YS /T 649-2018
	H65 C27000
4	GB /T 3114-1994
	H65 C27000

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!