A681 Type H14 T20814 - ASTM A681-2008(R2015)

Grade	A681 Type H14
USA UNS	T20814
AISI American Iron and Steel Institute	H14
Corresponding Standard	ASTM A681-2008(R2015) Standard Specification for Tool Steels Alloy
Classification	Alloy Steel

A681 Type H14 Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	W	More
Minimum Value	0.35	0.8	0.2	-	-	4.75	4	Ni+Cu≤0.75
Maximum Value	0.45	1.25	0.6	0.03	0.03	5.5	5.25	Ni+Cu≤0.75

A681 Type H14 Mechanical Properties

form	Heat Treatment or Condition	Hardness HBW
Bars, thick plates, thin plates, strips, rods, wires, forgings	Annealing	BHN ≤235
Bars, thick plates, thin plates, strips, rods, wires, forgings	Cold Drawing	BHN ≤262
Bars, thick plates, thin plates, strips, rods, wires, forgings	Heat Treatment	HRC ≥55

Approximate Comparison Table Cast Iron

China	United States	International Organization for Standardization	Germany		European Standard
GB	SAE	ISO	DIN EN/DIN	W-Nr.	EN	Numerical Grade
H195	H13 H14	JL HBW195 H195 H175	GG190HB	0.6022	EN-GJL-HB195	EN-JL2030

A681TypeH14 Corresponding Standards(Same grade name, different standards)