ZG35CrMnSi - HB 5001-1992

Grade	ZG35CrMnSi
Corresponding Standard	HB 5001-1992 Technical Standards for Structural Steel Investment Castings
Classification	Cast Steel

ZG35CrMnSi Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Ni	Cu	Mo ^*	W	V
Minimum Value	0.32	0.6	0.9	-	-	0.7	-	-	0.1	-	-
Maximum Value	0.4	0.9	1.2	0.035	0.03	1	0.4	0.3	0.2	0.4	0.2

ZG35CrMnSi Mechanical Properties

test	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Reduction of Area ψ %	Hardness HBW	Impact Energy Absorption KV2 J
Hot Cast Sample	890 ± 10°C Oil Quenching, 630~670°C Tempering	≥785	≥590	≥10	≥20	HB Indentation Diameter (mm): 4.05~3.65	≥24
Cold Cast Sample	890 ± 10°C Oil Quenching, 630~670°C Tempering	≥785	≥590	≥12	≥30	HB Indentation Diameter (mm): 4.05~3.65	≥31
Hot Cast Sample	890 ± 10°C Oil Quenching, 570~630°C Tempering	≥980	≥835	≥7	≥15	HB Indentation Diameter (mm): 3.65~3.35	≥16
Cold Cast Sample	890 ± 10°C Oil Quenching, 570~630°C Tempering	≥980	≥835	≥8	≥20	HB Indentation Diameter (mm): 3.65~3.35	≥20
Hot or cold cast sample	900±20°C Tempering	≥635	-	≥12	-	HB Indentation Diameter mm: 4.4~3.9	-

ZG35CrMnSi Corresponding Standards(Same grade name, different standards)

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!