GX4CrNi13-4 1.4317 - DIN EN 10293-2005

Grade	GX4CrNi13-4
Germany W-Nr.	1.4317
Corresponding Standard	DIN EN 10293-2005 Steel castings for general engineering uses
Classification	Cast Steel

GX4CrNi13-4 Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Ni	Mo
Minimum Value	-	-	-	-	-	12	3.5	-
Maximum Value	0.06	1	1	0.035	0.025	13.5	5	0.7

GX4CrNi13-4 Mechanical Properties

thickness t mm	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Impact Energy Absorption KV2 J
t≤300	Quenching + Tempering (+QT) Quenching temperature 1000~1050°C air cooling, Tempering temperature 590~620°C	760~960	≥550	≥15	≥50

Approximate Comparison Table Corrosion-Resistant Cast Steels

China

Taiwan, China

Japan

South Korea

United States

International Organization for Standardization

Germany

France

Russia

United Kingdom

ISC

CNS

JIS

ASTM

UNS

ISO

DIN EN/DIN

W-Nr.

NF EN/NF

GOST

BS EN/BS

ZG06Cr12Ni4

C54860

SCS 6

SCS 6X

SSC 6

CA6NM

J91540

GX4CrNi12-4

GX4CrNi13-4

1.4317

GX4CrNi13-4

08Х14Н7МЛ

425C12

GX4CrNi13-4 Corresponding Standards(Same grade name, different standards)

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!