EN-GJS-400-18-LT 5.3103 EN-GJS-400-18C-LT - EN 1563-2018

Grade	EN-GJS-400-18-LT
European Standard Steel Grade	5.3103
Other Names
Corresponding Standard	EN 1563-2018 Spheroidal Graphite Cast Irons
Classification	cast Iron
Density	7.1 g/cm³

EN-GJS-400-18-LT Mechanical Properties

condition	Mark	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Impact Energy Absorption KV2 J
Casting specimen; t≤30	EN-GJS-400-18-LT	≥400	≥240	≥18	(− 20 ± 2) °C Average of 3 samples: ≥12 Single sample value: ≥9
Casting specimen; 30<t≤60	EN-GJS-400-18-LT	≥380	≥230	≥15	(− 20 ± 2) °C Average of 3 samples: ≥12 Single sample value: ≥9
Casting samples; 60<t≤200	EN-GJS-400-18-LT	≥360	≥220	≥12	(−20 ± 2) °C Average value of 3 samples: ≥ 10 Individual sample value: ≥ 7
Base specimen; t≤30	EN-GJS-400-18C-LT	≥390	≥240	≥15
Base specimen; 30<t≤60	EN-GJS-400-18C-LT	≥370	≥230	≥12
Body sample; 60<t≤200	EN-GJS-400-18C-LT	≥340	≥220	≥10

• Samples cut from the casting the letter “C” is added at the end of the designation by symbol. e.g. EN-GJS-800-2C

Approximate Comparison Table Cast Iron

Japan	United States	International Organization for Standardization	Germany		France	European Standard		Sweden	United Kingdom
JIS	ASTM	ISO	DIN EN/DIN	W-Nr.	NF EN/NF	EN	Numerical Grade	SS	BS EN/BS
FCD400-18L	60-40-18	400-18 400-18-LT/S 400-18-LT/U 400-18L	GGG40.3	0.7043	400-18L20	EN-GJS-400-18-LT	5.3103 (EN-JS1025)	17-02	400/18L20