060A67 - BS 970-1-1983

Grade	060A67
Corresponding Standard	BS 970-1-1983 British Standard Specification for Wrough steels for mechanical and allied engineering purposes Part 1. General inspection and testing procedures and specific requirements for carbon,carbon manganese,alloy and stainless steels
Classification	Carbon Steel

060A67 Chemical Element Composition Content (%)

Component	C	Mn	P	S	Cr	Ni	Mo
Minimum Value	0.65	0.5	-	0.025	-	-	-
Maximum Value	0.7	0.7	0.05	0.05	0.3	0.4	0.15

• For older grades of stainless steel, see Table 2 of standard BS 970-4-1970

060A67 Mechanical Properties

diameter or across flats d mm	Heat Treatment or Condition	Hardness HBW
Hot rolled steel	Mill Condition and Softening	≤217

• Re-yield strength；Rp0.2-Stress at 0.2% proof plastic elongation (0.2% proof strength).
• Not specified, σs in the table refers to Re
• ft.lb=1.3558J

1 Approximate Comparison Table High-Quality Carbon Structural Steel

China		United States		International Organization for Standardization	Germany		France	Russia	Sweden	United Kingdom
GB	ISC	ASTM/AISI	UNS	ISO	DIN EN/DIN	W-Nr.	NF EN/NF	GOST	SS	BS EN/BS
65	U20652	1065	G10650	SL SM	Ck67	1.1231	XC65	65	1770	060A67

2 Approximate Comparison Table Spring Steel

China		Japan	United States		International Organization for Standardization	Germany		France	Russia	Sweden	United Kingdom
GB	ISC	JIS	AISI	UNS	ISO	DIN EN/DIN	W-Nr.	NF EN/NF	GOST	SS₁₄	BS EN/BS
65	U20652	SUP2	1065	G10650	Type DC	Ck67	1.1231	XC65	65	1770	060A67

3 Approximate Comparison Table High-Quality Carbon Structural Steel

China	United States	France	Russia	United Kingdom
GB	ASTM/AISI	NF EN/NF	GOST	BS EN/BS
65 (GB/T 699-1999)	1064 1065	C65 XC65	65	060A67

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!