Custom455 - H2ABC

Grade	Custom455
Brand/Supplier	America -> Carpenter
Classification	Martensitic Stainless Steel

Custom455 Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Ni	Cu	Mo	Ti	More
Minimum Value	-	-	-	-	-	11	7.5	1.5	-	0.8	Fe: 余量；Cb+Ta: 0.1~0.5
Maximum Value	0.05	0.5	0.5	0.04	0.03	12.5	9.5	2.5	0.5	1.4	Fe: 余量；Cb+Ta: 0.1~0.5

Custom455 Mechanical Properties

diameter or thickness d mm	Test Temperature	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Reduction of Area ψ %	Hardness HBW	Impact Energy Absorption KV2 J
Bars; d=25.4	Room Temperature	Annealing A	Rm: 1000 Rm,N(Kt=10): 1585	793	14	60	HRC: 31	95
Bars; d=25.4		H900	Rm: 1724 Rm,N(Kt=10): 1792	1689	10	45	HRC: 49	12
Bars; d=25.4		H950	Rm: 1620 Rm,N(Kt=10): 2068	1551	12	50	HRC: 48	19
Bars; d=25.4		H1000	Rm: 1448 Rm,N(Kt=10): 2000	1379	14	55	HRC: 45	27
Bars; d=25.4		H1050	Rm: 1310 Rm,N(Kt=10): 1793	1207	15	55	HRC: 40	48
Bar stock; d=102		Annealing A	965	793	12	50	HRC: 31	-
Bar stock; d=102		H950	Rm: 1585 Rm,N(Kt=10): 1723	1516	10	45	HRC: 48	11
Bar stock; d=102		H1000	Rm: 1413 Rm,N(Kt=10): 1723	1344	12	45	HRC: 45	16
Bar stock; d=102		H1050	Rm: 1309 Rm,N(Kt=10): 1723	1206	14	50	HRC: 40	34
Strip; d = 1.27		Annealing A	1103	1034	L0=50.8mm: 6	-	HRC: 34
Strip; d = 1.27		H900	1793	1724	L0=50.8mm: 3	-	HRC: 51
Strip; d = 1.27		H950	1724	1655	L0=50.8mm: 4	-	HRC: 47
Strip; d = 1.27		H1000	1517	1448	L0=50.8mm: 5	-	HRC: 44
Strip; d = 4.1		Annealing A	1103	930	L0=50.8mm: 8	54	HRC: 33
Strip; d = 4.1		H900	1792	1724	L0=50.8mm: 3	25	HRC: 51
Strip; d = 4.1		H950	1724	1655	L0=50.8mm: 4	40	HRC: 48
Strip; d = 4.1	Room Temperature	H1000	1517	1448	L0=50.8mm: 6	45	HRC: 46
Steel		H1000	Rm: 1517 Rm,N(Kt=10): 2068	-	13	50		22
Steel		H1000	Rm: 1758 Rm,N(Kt=10): 1517	-	13	45		7
Steel		H950	Rm: 1689 Rm,N(Kt=10): 1931	-	11	45		14
Steel		H950	Rm: 1931 Rm,N(Kt=10): 793	-	5	20		4
Steel		H950	1345	1276	12	50	Room Temperature HRC after Testing: 48
Steel		H950	1207	1124	14	60	Room Temperature HRC after Testing: 48
Steel		H950	896	758	18	70	Room Temperature HRC after Testing: 48
Steel		H900	1476	1372	10	49	Post-test room temperature HRC: 49
Steel		H900	1407	1296	11	50	Post-test room temperature HRC: 49
Steel		H900	1345	1241	12	52	Post-test room temperature HRC: 49
Steel		H900	1241	1145	14	56	Post-test room temperature HRC: 49
Steel		H1000	1200	1138	14	60	Room Temperature HRC after Testing: 44
Steel		H1000	1062	1020	15	65	Room Temperature HRC after Testing: 44
Steel		H1000	814	758	20	75	Room Temperature HRC after Testing: 44
Steel		H900	10h: Ru: 1034 100h: Ru: 827 1000h: Ru: 641
Steel		H950	10h: Ru: 979 100h: Ru: 807 1000h: Ru: 627
Steel		H950	10h: Ru: 752 100h: Ru: 565 1000h: Ru: 372

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!