080M36 - BS 970-1-1983

Grade	080M36
Corresponding Standard	BS 970-1-1983 British Standard Specification for Wrough steels for mechanical and allied engineering purposes Part 1. General inspection and testing procedures and specific requirements for carbon,carbon manganese,alloy and stainless steels
Classification	Carbon Steel

080M36 Chemical Element Composition Content (%)

Component	C	Mn	P	S	Cr	Ni	Mo
Minimum Value	0.32	0.6	-	0.015	-	-	-
Maximum Value	0.4	1	0.025	0.04	0.3	0.4	0.15

• For older grades of stainless steel, see Table 2 of standard BS 970-4-1970

080M36 Mechanical Properties

Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Hardness HBW
≥550	≥280	≥16	HB 152~207

• Re-yield strength；Rp0.2-Stress at 0.2% proof plastic elongation (0.2% proof strength).
• Not specified, σs in the table refers to Re
• ft.lb=1.3558J

1 Approximate Comparison Table High-Quality Carbon Structural Steel

China

Taiwan, China

Japan

South Korea

United States

International Organization for Standardization

Germany

France

Russia

Sweden

United Kingdom

ISC

CNS

JIS

ASTM/AISI

UNS

ISO

DIN EN/DIN

W-Nr.

NF EN/NF

GOST

BS EN/BS

U20352

S35C

SM35C

1035

G10350

C35E4

C35E
Ck35

1.1181

C35E
XC38

1572

C35E
080M36

2 Approximate Comparison Table Non-Alloy Steel for Quenching and Tempering

United States	International Organization for Standardization	Germany	France	European Standard		United Kingdom
ASTM	ISO	DIN EN/DIN	NF EN/NF	EN	Numerical Grade	BS EN/BS
1035	C35R C35M2	C35 Cm35	XC38H1u	C35R	1.1180	080M36

3 Approximate Comparison Table High-Quality Carbon Structural Steel

China	Japan	United States	International Organization for Standardization	Germany	France	European Standard		Russia	Sweden	United Kingdom
GB	JIS	ASTM	ISO	DIN EN/DIN	NF EN/NF	EN	Numerical Grade	GOST	SS	BS EN/BS
35	S35C	1035	C35E4	Ck35	XC38 XC38H1	C35E	1.1181	35	1572	080M36 CFS6

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!