30CrMnMoRE 603 - GJB 31A-2000

Grade	30CrMnMoRE
	603
Corresponding Standard	GJB 31A-2000 Specification for 30CrMnMoRE, 30CrNi2MnMoRE and 30CrNi3MoV Steel Plates for Armour Use
Classification	Alloy Steel

30CrMnMoRE Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Mo	Re
Minimum Value	0.26	0.3	1.05	-	-	0.8	0.6	0.07
Maximum Value	0.32	0.6	1.55	0.025	0.02	1.3	0.8	0.12

Note: RE is calculated according to the amount added and is not analyzed

30CrMnMoRE Mechanical Properties

thickness t mm	Hardness HBW
30~80	high tempering HBS10/300:≤269 indentation diameter≥3.7mm tempered fracture sample HBS10/300: 341~285 indentation diameter3.3~3.6mm
100	high tempering HBS10/300:≤269 indentation diameter≥3.7mm tempered fracture sample HBS10/300: 341~269 indentation diameter3.3~3.7mm

• Impact Absorption Energy:
The steel plate should be tested for Charpy V-notch impact energy at -40°C in the tempered condition. The impact absorption energy Akv (the average of two transverse specimens) should not be less than 30 J. The impact absorption energy results for 603 steel plates are not used as a basis for delivery.

• Heat treatment: Quenching temperature 900~930°C, holding time 2~3min/mm, water cooling; Tempering temperature 600~630°C, holding time 3~5min/mm, water cooling