N05500 - ASTM B 865-2004 - H2ABC

中文版

USA UNS	N05500
Corresponding Standard	ASTM B865-2004 Standard Specification for Precipitation Hardening Nickel-Copper-Aluminum Alloy (UNS N05500) Bar, Rod, Wire, Forgings, and Forging Stock
Classification	Alloy Steel
Properties	Strength Corrosion Resistance

Chemical Element Composition Content (%)

Component	Fe	C	Si	Mn	S	Ni	Cu	Al
Minimum Value	-	-	-	-	-	63	27	2.3
Maximum Value	2	0.18	0.5	1.5	0.01	-	33	3.15

Mechanical Properties

thickness t in(mm)	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Hardness HBW
All Sizes	hot-worked and age-hardened	≥965	≥690	≥20	HB3000: ≥265 HRC: ≥27
>1/4(6.4)~1(25.4)	Cold Processing + Age Hardening	≥1000	≥760	≥15	HB3000: ≥300 HRC: ≥32
>1(25.4)~3(76.2)	Cold Processing + Age Hardening	≥965	≥690	≥17	HB3000: ≥280 HRC: ≥29 ≥280
>3(76.2)~4(101.6)	Cold Processing + Age Hardening	≥930	≥655	≥20	HB3000: ≥255 HRC: ≥25
>1/4(6.4)~2(50.8)	Cold Processing + Age Hardening	≥965	≥690	≥15	HB3000: ≥265 HRC: ≥27
<1(25.4)	anneal and age-hardened*	≥895	≥620	≥20	HB3000: ≥250 HRC: ≥24
>1(25.4)	anneal and age-hardened*	≥895	≥895	≥20	HB3000: ≥250 HRC: ≥24

Approximate Comparison Table Corrosion-Resistant Alloy

China		United States		Germany
GB	ISC	Commercial Grade	UNS	W-Nr.
NS 6500 Ni68Cu28Al	H 05500	Monel K500	N 05500	2.4375

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!