A1200P 1200 - JIS H 4000-2022

Grade	A1200P
	1200
Corresponding Standard	JIS H 4000-2022 Aluminium and Aluminium Alloy Sheets, Strips and Plates
Classification	Aluminum and Aluminum Alloys

A1200P Chemical Element Composition Content (%)

Component	Mn	Cu	Ti	Al	Zn	Other Individual	Other Total	More
Minimum Value	-	-	-	99	-	-	-	Si+Fe≤1
Maximum Value	0.05	0.05	0.05	-	0.1	0.05	0.15	Si+Fe≤1

"Other individual elements or other totals": The chemical composition includes elements not specified in the table. Analysis should only be conducted if these elements are suspected to be present, or if routine analysis suggests that their content may exceed the prescribed limits.

A1200P Mechanical Properties

thickness t mm	Mark	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %
4≤t≤6.5	A1200P-H112	H112	≥95	≥50	≥9
6.5＜t≤13			≥90	≥50	≥9
13＜t≤50			≥85	≥35	≥14
50＜t≤75			≥80	≥25	≥20
0.2≤t≤0.5	A1200P-O	O	75~105	≥25	≥17
0.5＜t≤0.8			75~105	≥25	≥22
0.8＜t≤1.3			75~105	≥25	≥22
1.3＜t≤6.5			75~105	≥25	≥30
6.5＜t≤75			75~105	≥25	A50mm: ≥28 A: ≥25
0.2≤t≤0.3	A1200P-H12 A1200P-H22	H12 H22	95~125	≥75	≥2
0.3＜t≤0.5			95~125	≥75	≥3
0.5＜t≤0.8			95~125	≥75	≥4
0.8＜t≤1.3			95~125	≥75	≥6
1.3＜t≤2.9			95~125	≥75	≥8
2.9＜t≤12			95~125	≥75	≥9
0.2≤t≤0.3	A1200P-H14 A1200P-H24	H14 H24	120~145	≥95	≥1
0.3＜t≤0.5			120~145	≥95	≥2
0.5＜t≤0.8			120~145	≥95	≥3
0.8＜t≤1.3			120~145	≥95	≥4
1.3＜t≤2.9			120~145	≥95	≥5
2.9＜t≤12			120~145	≥95	≥6
0.2≤t≤0.5	A1200P-H16 A1200P-H26	H16 H26	135~165	≥115	≥1
0.5＜t≤0.8			135~165	≥115	≥2
0.8＜t≤1.3			135~165	≥115	≥3
1.3＜t≤4			135~165	≥115	≥4
0.2≤t≤0.5	A1200P-H18	H18	≥150	≥130	≥1
0.5＜t≤0.8			≥150	≥130	≥2
0.8＜t≤1.3			≥150	≥130	≥3
1.3＜t≤3.0			≥150	≥130	≥4

Approximate Comparison Table Wrought Aluminum and Aluminum Alloy

China	Japan	United States		International Organization for Standardization		France	European Standard	Russia
GB	JIS	ASTM	UNS	ISO	Numerical Grade	NF EN/NF	EN	GOST
1200	1200 A91200	1200	A91200	Al99.0	A91200	A4 1200 A91200	EN-AW-Al99.00	АД/1015