Grade A2014AP
2014A
Corresponding Standard JIS H 4000-2022
Aluminium and aluminium alloy sheets, strips and plates
Classification Aluminum and Aluminum Alloys
A2014AP Chemical Element Composition Content (%)
Component Fe Si Mn Cr Ni Cu Ti Zn Mg Other Individual Other Total More
Minimum Value - 0.5 0.4 - - 3.9 - - 0.2 - - Al: 余量；Zr+Ti≤0.2
Maximum Value 0.5 0.9 1.2 0.1 0.1 5 0.15 0.25 0.8 0.05 0.15
"Other individual elements or other totals": The chemical composition includes elements not specified in the table. Analysis should only be conducted if these elements are suspected to be present, or if routine analysis suggests that their content may exceed the prescribed limits.
A2014AP Mechanical Properties
thickness
t
mm		 Mark
Heat Treatment or Condition
Tensile Strength
σb
Mpa 		Yield Point
σs
Mpa 		Elongation or Extension Rate
δ
%
0.35≤t≤3.2 A2014AP-O O ≤220 ≤140 A50mm: ≥16
A: ≥13
3.2＜t≤12.5 ≤220 ≤140 A50mm: ≥16
A: ≥12
12.5＜t≤25 ≤220 ≤140 A50mm: ≥12
A: ≥9
0.35≤t≤6.3 A2014AP-T3
A2014AP-T4		 T3
T4		 ≥395 ≥240 ≥14
6.3＜t≤12 ≥395 ≥235 ≥13
0.35≤t≤1 A2014AP-T6 T6 ≥440 ≥380 ≥6
1＜t≤1.6 ≥440 ≥380 ≥7
1.6＜t≤12 ≥440 ≥390 ≥7
6≤t≤12 A2014AP-T451 T451 ≥395 ≥240 ≥14
12＜t≤12.5 ≥400 ≥250 ≥14
12.5＜t≤25 ≥400 ≥250 A50mm: ≥14
A: ≥12
25＜t≤40 ≥400 ≥250 A: ≥10
40＜t≤50 ≥400 ≥250 A: ≥8
50＜t≤60 ≥395 ≥250 A: ≥7
60＜t≤80 ≥390 ≥240 A: ≥7
6≤t≤12.5 A2014AP-T651 T651 ≥450 ≥395 ≥7
12.5＜t≤25 ≥460 ≥405 A50mm: ≥7
A: ≥6
25＜t≤40 ≥460 ≥405 A: ≥5
40＜t≤60 ≥450 ≥390 A: ≥3
60＜t≤80 ≥435 ≥380 A: ≥1
80＜t≤100 ≥405 ≥350 A: ≥1
Approximate Comparison Table Wrought Aluminum and Aluminum Alloy
China Japan United States International Organization for Standardization France European Standard United Kingdom
GB JIS ASTM UNS ISO Numerical Grade NF EN/NF EN Commercial Grade BS EN/BS
2014A 2014A
A92014 		2014A A92014 AlCu4SiMgMn(A) A92014 A-U4SG(A)
2014
A92014 		EN-AW-AlCu4SiMg(A) H15 2014A