Commercial Grade
Brand/Supplier	-> OUTOKUMPU
Classification	Duplex Stainless Steel

Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Ni	Cu	Mo	N	W	More
Minimum Value	-	-	-	-	-	24	6	0.5	3	0.2	0.5	PREN=Cr+3.3×Mo+16×N≥40
Maximum Value	0.03	1	1	0.03	0.01	26	8	1	4	0.3	1	PREN=Cr+3.3×Mo+16×N≥40

Mechanical Properties

condition	Test Temperature	Tensile Strength σ_b ksi	Specified Plastic Yield Strength Rp_0.2 ksi	Yield Point σ_s ksi	Elongation or Extension Rate δ %	Hardness HBW
ASTM A240	Room Temperature	≥109	≥80	≥550	≥25	HRC: ≤28
forged part, bar, plate; ≤ 1.2		109	80
forged part, bar, plate; ≤ 1.2		105	73
forged part, bar, plate; ≤ 1.2		102	68
forged part, bar, plate; ≤ 1.2		99	65
forged part, bar, plate; ≤ 1.2		97	62
forged part, bar, plate; ≤ 1.2		94	58
forged part, bar, plate; ≤ 1.2		92	56
plate; 1.2 ~ 2.75		109	80
plate; 1.2 ~ 2.75		102	68
plate; 1.2 ~ 2.75		97	62
plate; 1.2 ~ 2.75		90	58
plate; 1.2 ~ 2.75		88	55
plate; 1.2 ~ 2.75		87	54
plate; 1.2 ~ 2.75		86	52

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!