S620Q 1.8914 - EN 10025-6-2019(+A1:2022)

Grade	S620Q
European Standard Steel Grade	1.8914
Corresponding Standard	EN 10025-6-2019(+A1:2022) Hot Rolled Products of Structural Steels - Part 6: Technical Delivery Conditions for Flat Products of High Yield Strength Structural Steels in The Quenched and Tempered Condition
Classification	Alloy Steel
Properties	High Strength

S620Q Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Ni	Cu	Mo	N	Ti ^*	V ^*	Nb ^*	Zr ^*	B
Minimum Value	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-
Maximum Value	0.2	0.8	1.7	0.025	0.015	1.5	4	0.5	0.7	0.015	0.05	0.12	0.06	0.15	0.005

S620Q Mechanical Properties

condition	Test Temperature	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Impact Energy Absorption KV2 J
Hot-rolled plates; 3≤t≤50	Room Temperature	Tempering (Q)	700~890	ReH: ≥620	≥15
Hot-rolled plates; 50<t≤100	Room Temperature	Tempering (Q)	700~890	ReH: ≥580	≥15
Hot rolled plates; 100<t≤200	Room Temperature	Tempering (Q)	650~830	ReH: ≥560	≥15
Hot rolled plate						long. ≥40 tr. ≥30
Hot rolled plate						long. ≥30 tr. ≥27

1 Approximate Comparison Table Structural, Pressure Vessel and Engineering Steels

2 Approximate Comparison Table High strength structural steel plates in the quenched and tempered condition

S620Q Corresponding Standards(Same grade name, different standards)

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!