Grade X3CrNiCu19-9-2
ISO Numeric Designation 4560-304-75-E
Corresponding Standard ISO 4954-2-2024
Steels for cold heading and cold extruding — Technical delivery conditions — Part 2: Stainless steels
Classification Austenitic Stainless Steel
Properties Corrosion Resistance
X3CrNiCu19-9-2 Chemical Element Composition Content (%)
Component C Si Mn P S Cr Ni Cu N
Minimum Value - - 1.5 - - 18 8 1.5 -
Maximum Value 0.035 1 2 0.045 0.015 19 9 2 0.1
X3CrNiCu19-9-2 Mechanical Properties
diameter
d
mm		 Heat Treatment or Condition
Tensile Strength
σb
Mpa 		Reduction of Area
ψ
%
5＜d≤50 +AT or +AT+PE ≤610 ≥68
5＜d≤10 +AT+C ≤800 -
10＜d≤25 ≤750 -
2≤d≤5 +AT+C+AT ≤630 ≥68
5＜d≤25 ≤610 ≥68
2≤d≤5 +AT+C+AT+LC ≤720 ≥63
5＜d≤10 ≤660 ≥63
• +AT or +AT+PE=Solution annealed or solution annealed + peeled；+AT+C=Solution annealed + cold drawn；+AT+C+AT=Solution annealed + cold drawn + Solution annealed；+AT+C+AT+LC=Solution annealed + cold drawn + Solution annealed + skin passed；+A or +A+PE=Soft annealed or soft annealed + peeled；+A+LC=soft annealed + skin passed；+A+C+A=soft annealed + cold drawn + soft annealed；+A+C+A+LC=soft annealed + cold drawn + soft annealed + skin passed
Approximate Comparison Table Stainless Steels for Cold Heading and Cold Extruding
International Organization for Standardization European Standard
ISO Numerical Grade EN Numerical Grade
X3CrNiCu19-9-2 4560-304-75-E X3CrNiCu19-9-2 1.4560
X3CrNiCu19-9-2 Corresponding Standards(Same grade name, different standards)
1 EN 10088-1-2005
X3CrNiCu 19-9-2 1.4560
2 EN 10263-5-2001
X3CrNiCu19-9-2 1.4560
3 EN 10088-3-2014
X3CrNiCu 19-9-2 1.4560
4 ISO 15510-2014
X3CrNiCu19-9-2 4560-304-75-E
5 DIN EN 10263-5-2018
X3CrNiCu19-9-2 1.4560
6 DIN EN 10088-3-2014
X3CrNiCu 19-9-2 1.4560
7 ISO 4954-2018
X3CrNiCu19-9-2 4560-304-75-E
8 NF EN 10088-1-2005
X3CrNiCu19-9-2 1.4560
9 EN 10263-5-2017
X3CrNiCu19-9-2 1.4560
10 ISO 4954-2-2024
X3CrNiCu19-9-2 4560-304-75-E

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!