GH4080A H40801 GH80A - GB /T 14994-2008

Grade	GH4080A
China ISC	H40801
Old Grade
Corresponding Standard	GB /T 14994-2008 Superalloy Cold Drawn Bars
Classification	Alloy Steel
Properties	Corrosion Resistance High-Temperature Resistance
Density	8.19 g/cm³

GH4080A Chemical Element Composition Content (%)

Component	Fe	C	Si	Mn	P	S	Cr	Cu	Ti	B	Co	Pb	Al	Bi	Ag	More
Minimum Value	-	0.04	-	-	-	-	18	-	1.8	-	-	-	1	-	-	Ni：余量
Maximum Value	1.5	0.1	0.8	0.4	0.02	0.015	21	0.2	2.7	0.008	2	0.002	1.8	0.0001	0.0005	Ni：余量

GH4080A Mechanical Properties

test temperature °C	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Hardness HBW
Room Temperature	Solution Treatment + Aging Treatment	≥1000	≥620	≥20	≥285
	Solution treatment (delivery state)				≤325
	Cold drawn condition (delivery condition)				≤365

1 Approximate Comparison Table Deformed High-Temperature Alloy

2 Approximate Comparison Table Deformed High-Temperature Alloy

China	United States	International Organization for Standardization	European Standard
GB	SAE	ISO	EN	Numerical Grade
GH4080A 80A①	HEV5	NiCr20TiAl	NiCr20TiAl	2.4952

GH4080A Corresponding Standards(Same grade name, different standards)

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!