SFNCM 980R SFNCM 100R - JIS G 3222-1988

Grade	SFNCM 980R
Old Grade
Corresponding Standard	JIS G 3222-1988 Nickel Chromium Molybdenum Steel Forgings for General Use
Classification	Alloy Steel

SFNCM 980R Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Ni	Mo
Minimum Value	-	0.15	0.35	-	-	0.4	0.4	0.15
Maximum Value	0.5	0.35	1	0.03	0.03	3.5	3.5	0.7

① Cu as an impure content. shall not exceed 0.03 % .
② The chemical composition can be determined through negotiation between the buyer and the manufacturer within the range shown in the table.

SFNCM 980R Mechanical Properties

thickness t mm	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Reduction of Area ψ %	Hardness HBW	Impact Energy Absorption KV2 J
t≤100	980~1130	≥805	≥12	≥33	HB：≥285 HS：≥42	Impact value tangential ≥54 J/cm²
100＜t≤200	980~1130	≥785	≥11	≥32	HB：≥285 HS：≥42	Impact value tangential ≥49 J/cm²
200＜t≤300	980~1130	≥765	≥10	≥32	HB：≥285 HS：≥42	Impact value tangential ≥49 J/cm²

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!