МНЖМц30-1-1 MNZHMts30-1-1 - GOST 10092-2006

Grade	МНЖМц30-1-1
Other Names
Corresponding Standard	GOST 10092-2006 Cupro-Nickel Tubes for Heat-Exchange Apparatus. Specifications
Classification	Copper and Copper Alloys

МНЖМц30-1-1 Chemical Element Composition Content (%)

Component	Fe	C	Si	Mn	P	S	Pb	Zn	Other Total	More
Minimum Value	0.5	-	-	0.5	-	-	-	-	-	Ni+Co:29~33；Cu:Remainder
Maximum Value	1	0.05	0.15	1	0.006	0.01	0.05	0.5	0.6	Ni+Co:29~33；Cu:Remainder

"Other individual elements or other totals": The chemical composition includes elements not specified in the table. Analysis should only be conducted if these elements are suspected to be present, or if routine analysis suggests that their content may exceed the prescribed limits.

• The cobalt content does not exceed 0.5% to ensure the nickel content.

МНЖМц30-1-1 Mechanical Properties

condition	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Specified Plastic Yield Strength Rp_0.2 Mpa	Elongation or Extension Rate δ %	Hardness HBW
Tube	Soft (P)	≥350	≥120	δ5: ≥35 δ10: ≥30
Tube	Soft (H)				HV10: 90~130
Tube	1/2 Hard (P)	≥450	≥300	δ5: ≥12 δ10: ≥10
Tube	1/2 Hard (H)				HV10: ≥130

• P - Tensile test - to determine σb, δ5, δ10
• H - Hardness test HV10.

Approximate Comparison Table Wrought Cupronickel

China		United States		International Organization for Standardization		Germany		European Standard		Russia	Sweden
GB	ISC	ASTM	UNS	ISO	Numerical Grade	DIN EN/DIN	W-Nr.	EN	Numerical Grade	GOST	SS
BFe30-1-1	T71510	68Cu-30Ni-1Mn-.5Fe	C71581	CuNi30Fe1Mn	C71581	CuNi30Fe1Mn	C71581 2.0882	CuNi30Fe1Mn	CW354H	МНЖМц30-1-1	5682 C71581