МНЖМц10-1-1 MNZHMts10-1-1 - GOST 10092-2006

Grade	МНЖМц10-1-1
Other Names
Corresponding Standard	GOST 10092-2006 Cupro-nickel tubes for heat-exchange apparatus. Specifications
Classification	Copper and Copper Alloys
Density	8.9 g/cm³

МНЖМц10-1-1 Chemical Element Composition Content (%)

Component	Fe	C	Mn	S	Pb	Zn	Other Total	More
Minimum Value	1	-	0.3	-	-	-	-	Ni+Co:9~11；Cu:Remainder
Maximum Value	2	0.03	1	0.03	0.03	0.3	0.5	Ni+Co:9~11；Cu:Remainder

"Other individual elements or other totals": The chemical composition includes elements not specified in the table. Analysis should only be conducted if these elements are suspected to be present, or if routine analysis suggests that their content may exceed the prescribed limits.

• The cobalt content does not exceed 0.5% to ensure the nickel content.

МНЖМц10-1-1 Mechanical Properties

condition	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Specified Plastic Yield Strength Rp_0.2 Mpa	Elongation or Extension Rate δ %	Hardness HBW
Tube	Soft (P)	≥290	≥90	δ5: ≥35 δ10: ≥30
Tube	Soft (H)				HV10: 75~105
Tube	1/2 Hard (P)	≥310	≥220	δ5: ≥12 δ10: ≥10
Tube	1/2 Hard (H)				HV10: 105~150
Tube	Hard (H)	≥420	≥400	δ5: ≥5 δ10: ≥3
Tube	Hard (H)				HV10: ≥150

• P - Tensile test - to determine σb, δ5, δ10
• H - Hardness test HV10.

Approximate Comparison Table Wrought Cupronickel

China		United States		International Organization for Standardization		Germany		European Standard		Russia	Sweden
GB	ISC	ASTM	UNS	ISO	Numerical Grade	DIN EN/DIN	W-Nr.	EN	Numerical Grade	GOST	SS
BFe10-1-1	T70590	88Cu-10Ni-1.4Fe-.5Mn	C70600	CuNi10Fe1Mn	C70600	CuNi10Fe1Mn	C70600 2.0872	CuNi10Fe1Mn	CW352H	МНЖМц10-1-1	5667 C70600

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!