Grade Haynes R-41
Brand/Supplier
America -> HAYNES
Classification Nickel and Nickel Alloys
Density 8.25 g/cm3
Haynes R-41 Chemical Element Composition Content (%)
Component Fe C Si Mn Cr Ni Mo Ti Zr B Co Al
Minimum Value - - - - - - - - - - - -
Maximum Value 5 - 0.5 0.1 - - - - 0.07 - - -
Nominal Value - 0.09 - - 19 52 10 3.1 - 0.006 11 1.5
Haynes R-41 Mechanical Properties
condition Test Temperature Heat Treatment or Condition
Tensile Strength
σb
Mpa 		Specified Plastic Yield Strength
Rp0.2
Mpa 		Elongation or Extension Rate
δ
%
Alloy RT 1121°C /30 min./RAC + 899°C /4h/AC 1253 803 4D
20.5
Alloy 204°C 1121°C /30 min./RAC + 899°C /4h/AC 1201* 752* 16.5*
Alloy 427°C 1121°C /30 min./RAC + 899°C /4h/AC 1114* 752* 20.3*
Alloy 538°C 1121°C /30 min./RAC + 899°C /4h/AC 1110 739 21.2
Alloy 649°C 1121°C /30 min./RAC + 899°C /4h/AC 1192 743 19.3
Alloy 760°C 1121°C /30 min./RAC + 899°C /4h/AC 959 788 28.3
Alloy 816°C 1121°C /30 min./RAC + 899°C /4h/AC 798* 717* 27.2*
Alloy 871°C 1121°C /30 min./RAC + 899°C /4h/AC 615 550 28.5
Alloy 927°C 1121°C /30 min./RAC + 899°C /4h/AC 461* 407* 24.8*
Alloy 982°C 1121°C /30 min./RAC + 899°C /4h/AC 277 236 31.1
Alloy 1093°C 1121°C /30 min./RAC + 899°C /4h/AC 59* 34* 94.4*
Alloy RT 760°C /16h/AC 1416 1064 22.3
Alloy 204°C 760°C /16h/AC 1367* 974* 23*
Alloy 427°C 760°C /16h/AC 1252* 978* 25.6*
Alloy 538°C 760°C /16h/AC 1259 964 20.5
Alloy 649°C 760°C /16h/AC 1353 954 23.4
Alloy 760°C 760°C /16h/AC 1040 869 17.9
Alloy 816°C 760°C /16h/AC 883 774 19.4
Alloy 871°C 760°C /16h/AC 679 578 31.4
Alloy 927°C 760°C /16h/AC 430 352 38.7
Alloy 982°C 760°C /16h/AC 238 179 42.7

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!