Home Material GB /T 4232-2019
简体 | 繁體
Grade ML12Cr13
China ISC S41010
Old Grade
Corresponding Standard GB /T 4232-2019
Stainless Steel Wire for Cold Heading and Cold Forging
Classification Martensitic Stainless Steel
Properties Corrosion Resistance Forgability
ML12Cr13 Chemical Element Composition Content (%)
Component C Si Mn P S Cr Ni
Minimum Value 0.08 - - - - 11.5 -
Maximum Value 0.15 1 1 0.04 0.03 13.5 0.6
ML12Cr13 Mechanical Properties
diameter
d
mm		 Heat Treatment or Condition
Tensile Strength
σb
Mpa 		Elongation or Extension Rate
δ
% 		Reduction of Area
ψ
%
d=0.8~3.0 Soft (S) 440~640 - ≥55
d>3.0~11.0 Soft (S) 400~600 ≥15 ≥55
d=0.8~3.0 Light Drawing (LD) ≤740 - ≥50
d>3.0~20.0 Light Drawing (LD) ≤740 ≥10 ≥50
1 Approximate Comparison Table Martensitic Stainless Steel
China Taiwan, China Japan South Korea United States International Organization for Standardization Germany France European Standard Russia Sweden United Kingdom
GB ISC CNS JIS KS ASTM UNS ISO Numerical Grade DIN EN/DIN W-Nr. NF EN/NF EN Numerical Grade GOST SS BS EN/BS
12Cr13
(1Cr13) 		S41010 410 SUS 410 STS 410 410 S41000 X12Cr 13 4006-410-00-I X10Cr 13
X12Cr 13 		1.4006
1.4006 		Z12C 13
Z10C13 		X12Cr 13 1.4006 12Х13
12KH13
15KH13L 		2302 410S21
2 Approximate Comparison Table Martensitic Heat-Resistant Steel
China Taiwan, China Japan South Korea United States International Organization for Standardization Germany France European Standard Russia Sweden United Kingdom
GB ISC CNS JIS KS ASTM UNS ISO DIN EN/DIN W-Nr. NF EN/NF EN Numerical Grade GOST SS BS EN/BS
12Cr13
(1Cr13) 		S41010 410 SUS 410 STS 410 410 S41000 X12Cr 13
3
(ISO 683-13-1986) 		X10Cr 13 1.4006 Z12C 13 X12Cr 13 1.4006 12Х13 2302 410S21
3 Approximate Comparison Table Stainless Steels for Cold Heading and Cold Extruding
China Japan United States International Organization for Standardization European Standard
GB ISC JIS ASTM/AISI UNS ISO Numerical Grade EN Numerical Grade
12Cr13
(1Cr13) 		S41010 SUS410 410 S41000 X12Cr13 4006-410-00-I X12Cr13 1.4006

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!