CuAl10Fe1 CW305G - EN 12167-2024

Grade	CuAl10Fe1
European Standard Steel Grade	CW305G
Corresponding Standard	EN 12167-2024 Copper and copper alloys - Profiles and bars for general purposes
Classification	Copper and Copper Alloys
Density	7.6 g/cm³

CuAl10Fe1 Chemical Element Composition Content (%)

Component	Fe	Si	Mn	Ni	Pb	Al	Zn	Sn	Other Total	More
Minimum Value	0.5	-	-	-	-	9	-	-	-	Cu_min:Rem.
Maximum Value	1.5	0.2	0.5	1	0.02	10	0.5	0.1	0.2	Cu_min:Rem.

"Other individual elements or other totals": The chemical composition includes elements not specified in the table. Analysis should only be conducted if these elements are suspected to be present, or if routine analysis suggests that their content may exceed the prescribed limits.

CuAl10Fe1 Mechanical Properties

thickness t mm	Mark	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Specified Plastic Yield Strength Rp_0.2 Mpa	Elongation or Extension Rate δ %	Hardness HBW
3≤t≤6	CuAl10Fe1-R630	R630	≥630	≥490	≥4(A100), ≥5(A11.3)
6<t≤30	CuAl10Fe1-R530	R530	≥530	≥290	≥8(A11.3), ≥10(A)
3≤t≤6	CuAl10Fe1-H155	H155				≥155
6<t≤10	CuAl10Fe1-H130	H130				130~170
All specifications	CuAl10Fe1-M	M	As manufactured	As manufactured	As manufactured	As manufactured

Test pieces shall be in accordance with EN ISO 6892-1:2019, except that 200 mm gauge length is not permitted.
Elongation requirements for rod of thickness or diameter equivalent to the cross sectional area:
ⓐ less than 4 mm (A100 mm);
ⓑ 4 mm up to and including 8 mm (A 11,3);
ⓒ greater than 8 mm (A);

CuAl10Fe1 Corresponding Standards(Same grade name, different standards)

1	EN 12163-1998
	CuAl10Fe1 CW305G
2	DIN EN 12163-1998
	CuAl10Fe1 CW305G
3	DIN EN 12163-2016
	CuAl10Fe1 CW305G
4	EN 12163-2016
	CuAl10Fe1 CW305G
5	EN 12167-2024
	CuAl10Fe1 CW305G

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!