1100 - GB /T 3195-2016

Grade	1100
Corresponding Standard	GB /T 3195-2016 Aluminium and aluminium alloys drawn round wires
Classification	Aluminum and Aluminum Alloys

1100 Chemical Element Composition Content (%)

Component	Mn	Cu	Al	Zn	Other Individual	Other Total	More
Minimum Value	-	0.05	99	-	-	-	(Si+Fe)≤0.95
Maximum Value	0.05	0.2	-	0.1	0.05	0.15	(Si+Fe)≤0.95

"Other individual elements or other totals": The chemical composition includes elements not specified in the table. Analysis should only be conducted if these elements are suspected to be present, or if routine analysis suggests that their content may exceed the prescribed limits.

Chemical composition according to GB/T 3190-2008

1100 Mechanical Properties

diameter d mm	Mark	Heat Treatment or Condition	Tensile Strength σ_b Mpa
1.6~25	1100-O	Annealing (O)	≤110
1.6~25	1100-H14	Work hardening-1/2 hard (H14)	110~145

①T6-solution heat treatment and artificial aging

Approximate Comparison Table Wrought aluminum and aluminum alloy

China	Japan	United States		International Organization for Standardization		France	European Standard	Russia
GB	JIS	ASTM	UNS	ISO	Numerical Grade	NF EN/NF	EN	GOST
1100	1100 A91100	1100	A91100	Al99.0Cu	A91100	A45 1100 A91100	EN-AW-Al99.0Cu	АД

1100 Corresponding Standards(Same grade name, different standards)

1	JIS H 4040-2006
	1100 A 1100 W A 1100 BD A 1100 BE
2	GB /T 3195-2016
	1100
3	GB /T 3190-2020
	1100
4	JIS H 4160-1994(R2005)
	1100
5	GB /T 3880.1-2012
	1100
6	JIS H 4000-2022
	1100 A1100P

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!