S460B - ISO 630-2-2021

Grade	S460B
Corresponding Standard	ISO 630-2-2021 Structural Steels - Part 2: Technical Delivery Conditions for Structrual Steels for General Purposes
Classification	Alloy Steel

S460B Chemical Element Composition Content (%)

	Component	C ^*	Si	Mn	P	S	Cu	N	Ti	V	Nb
t≤40	Minimum Value	-	-	-	-	-	-	-	-	-	-
t≤40	Maximum Value	0.2	0.55	1.7	0.03	0.03	0.55	0.025	0.05	0.13	0.05

	Component	C	Si	Mn	P	S	Cu	N	Ti	V	Nb
t＞40	Minimum Value	-	-	-	-	-	-	-	-	-	-
t＞40	Maximum Value	0.22	0.55	1.7	0.03	0.03	0.55	0.025	0.05	0.13	0.05

• The table shows the chemical composition of heat analysis.

① FN = rimming steels not permitted; FF = fully killed steel. t=nominal thickness in mm
② For sections with nominal thickness > 100 mm, the C content is by agreement.
③ For long products, the P and S content may be 0,005 % higher.
④ For long products, the max. S content may be increased for improved machinability by 0,015 % by agreement if the steel is treated to modify the sulfide morphology, and if the chemical composition shows min. 0,002 0 % Ca.
⑤ The maximum value for nitrogen does not apply if the chemical composition shows a minimum total Al content of 0,020 % or, alternatively, minimum 0,015 % acid-soluble Al or if sufficient other N-binding elements are present. In this case, the N-binding elements shall be mentioned in the inspection document.
⑥ Cu content above 0,40 % can cause hot shortness during hot forming.
⑦ If other elements are added, they shall be mentioned on the inspection document.
* For nominal thickness t＞30mm：C=0.22% max.
◎ Applicable for long products only.

S460B Mechanical Properties

thickness t mm	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Impact Energy Absorption KV2 J
t≤16	550~720	ReH: ≥460	long.: ≥17	20°C: ≥27
16＜t≤40	550~720	ReH: ≥440	long.: ≥17	20°C: ≥27
40＜t≤63	550~720	ReH: ≥420	long.: ≥17	20°C: ≥27
63＜t≤80	550~720	ReH: ≥400	long.: ≥17	20°C: ≥27
80＜t≤100	550~720	ReH: ≥390	long.: ≥17	20°C: ≥27
100＜t≤150	530~700	ReH: ≥390	long.: ≥17	20°C: ≥27

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!