C5D2 1.1111 - EN 10016-4-1994

Grade	C5D2
European Standard Steel Grade	1.1111
Corresponding Standard	EN 10016-4-1994 Non-Alloy Steel Rod for Drawing and/or Cold Rolling — Part 4: Specific Requirements for Rod for Special Applications
Classification	Carbon Steel

C5D2 Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Ni	Cu	Mo	N	Al	More
Minimum Value	-	-	0.3	-	-	-	-	-	-	-	-	Cr+Ni+Cu ≤ 0.3%；Cu+Sn ≤ 0.15%
Maximum Value	0.07	0.3	0.5	0.02	0.025	0.1	0.1	0.15	0.05	0.007	0.01	Cr+Ni+Cu ≤ 0.3%；Cu+Sn ≤ 0.15%

• Elements not included in this table may not be added intentionally to the steel without the agreement of the purchaser, except those intended for finishing the cast.
• The addition of microalloying elements can be agreed between the manufacturer and purchaser at the time of ordering.
• Special non-alloy steel according to EN 10020.
• For rod intended for galvanization the allowed lower limit of silicon content should be specified at the time of ordering.
• For the maganese content, a different range from the one indicated in the table can be agreed at the time of ordering with a maximum value not exceeding 1,20 % and with an amplitude of 0,20 %.
• For certain applications the Cu content may be restricted to 0,12 % max, by agreement.
• By agreement at the time of ordering, the value for aluminium can be fixed at 0,02 to 0,06 %. The value for silicon can then be fixed at k 0,10 % on request.
• If, in accordance the Al content is fixed at 0,02 to 0,06 %, the limit value for N shall be agreed at the time of ordering.

C5D2 Corresponding Standards(Same grade name, different standards)

1	NF EN 10016-4-1995
	C5D2
2	EN 10016-4-1994
	C5D2 1.1111