1100 A 1100 W A 1100 BD - JIS H 4040-2006

Grade	1100
Other Names
Corresponding Standard	JIS H 4040-2006 Aluminium and aluminium alloy rods, bars and wires
Classification	Aluminum and Aluminum Alloys
Properties	Corrosion Resistance Weldability

1100 Chemical Element Composition Content (%)

Component	Be	Mn	Cu	Al	Zn	Other Individual	Other Total	More
Minimum Value	-	-	0.05	99	-	-	-	Si+Fe ≤ 0.95；
Maximum Value	0.0003	0.05	0.2	-	0.1	0.05	0.15	Si+Fe ≤ 0.95；

"Other individual elements or other totals": The chemical composition includes elements not specified in the table. Analysis should only be conducted if these elements are suspected to be present, or if routine analysis suggests that their content may exceed the prescribed limits.

1100 Mechanical Properties

condition	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %
Drawn Rod, Wire; d ≤ 3	Annealing (O)	75~110
Drawn Rod, Wire; 3 < d ≤ 100	Annealing (O)	75~110	≥20	≥25
Drawn Rod, Wire; d ≤ 30	Strain-hardening - 1/2 hard (H14)	≥110	≥80	≥5
Drawn Rod, Wire; d ≤ 10	Strain - Hardening - 4/4 Hard (H18)	≥150	≥130	≥3
Extruded Round (Rectangular, Square, and Hexagonal) Bars; d < 35 (30)	Strain - Only Hardening (H112)	≥75	≥20	≥18
Extruded Round (Rectangular, Square, and Hexagonal) Bars; d ≥ 35 (30)	Strain - Only Hardening (H112)	≥75	≥20

d: diameter, thickness or width across flats；unit mm
s: cross section area; unit cm²
A、A50mm-gauge length

Approximate Comparison Table Wrought aluminum and aluminum alloy

China	Japan	United States		International Organization for Standardization		France	European Standard	Russia
GB	JIS	ASTM	UNS	ISO	Numerical Grade	NF EN/NF	EN	GOST
1100	1100 A91100	1100	A91100	Al99.0Cu	A91100	A45 1100 A91100	EN-AW-Al99.0Cu	АД

1100 Corresponding Standards(Same grade name, different standards)

1	JIS H 4040-2006
	1100 A 1100 W A 1100 BD A 1100 BE
2	GB /T 3195-2016
	1100
3	GB /T 3190-2020
	1100
4	JIS H 4160-1994(R2005)
	1100
5	GB /T 3880.1-2012
	1100
6	JIS H 4000-2022
	1100 A1100P

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!