2219 A2219 BD A2219 BDS - JIS H 4040-2006

Grade	2219
Other Names
Corresponding Standard	JIS H 4040-2006 Aluminium and aluminium alloy rods, bars and wires
Classification	Aluminum and Aluminum Alloys
Properties	High Strength Good Weldability

2219 Chemical Element Composition Content (%)

Component	Fe	Si	Mn	Cu	Ti	V	Zr	Zn	Mg
Minimum Value	-	-	0.2	5.8	0.02	0.05	0.1	-	-
Maximum Value	0.3	0.2	0.4	6.8	0.1	0.15	0.25	0.1	0.02

2219 Mechanical Properties

diameter,thickness or width arcoss flats d mm	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %
10≤d≤50	Drawing rod solution treatment + cold working + artificial aging (T851) ≥400	Drawing rod solution treatment + cold working + artificial aging (T851) ≥275	Elongation Percentage at L0=5.65√So ≥3
50≤d≤100	≥395	≥270	≥3

d: diameter, thickness or width across flats；unit mm
s: cross section area; unit cm²
A、A50mm-gauge length

Approximate Comparison Table Wrought Aluminum and Aluminum Alloy

China	Japan	United States		International Organization for Standardization		France	European Standard	Russia
GB	JIS	ASTM	UNS	ISO	Numerical Grade	NF EN/NF	EN	GOST
2219	2219 A92219	2219	A92219	AlCu6Mn	A92219	A-U6M 2219 A92219	EN-AW-AlCu6Mn	1201

2219 Corresponding Standards(Same grade name, different standards)

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!