2011 A2011 W A2011 BD - JIS H 4040-2006

Grade	2011
	A2011 W
Other Names
Corresponding Standard	JIS H 4040-2006 Aluminium and aluminium alloy rods, bars and wires
Classification	Aluminum and Aluminum Alloys
Properties	Strength Machinability

2011 Chemical Element Composition Content (%)

Component	Fe	Si	Cu	Pb	Zn
Minimum Value	-	-	5	0.2	-
Maximum Value	0.7	0.4	6	0.6	0.3

2011 Mechanical Properties

diameter d mm	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %
3≤d≤38	Drawing rod / wire solution treatment + cold working + natural aging (T3) ≥310	Drawing rod / wire solution treatment + cold working + natural aging (T3) ≥260	At a length of 5.65√So ≥10
38＜d≤50	≥295	≥235	≥12
50＜d≤80	≥280	≥205	≥14
3≤d≤80	Drawing rod / wire solution treatment + cold working + artificial aging (T8) ≥370	Drawing rod / wire solution treatment + cold working + artificial aging (T8) ≥270	At a length of 5.65√So ≥10

d: diameter, thickness or width across flats；unit mm
s: cross section area; unit cm²
A、A50mm-gauge length

Approximate Comparison Table Wrought aluminum and aluminum alloy

China	Japan	United States		International Organization for Standardization		Germany		European Standard
GB	JIS	ASTM	UNS	ISO	Numerical Grade	DIN EN/DIN	W-Nr.	EN
2011	2011 A92011	2011	A92011	AlCu6BiPb	A92011	EN-AW-AlCu6BiPb	3.1655 A92011	EN-AW-AlCu6BiPb