E460 E - JIS G 3128-1999(R2004)

Grade	E460 E
Corresponding Standard	JIS G 3128-1999(R2004) High Yield Strength Steel Plates for Welded Structure
Classification	Alloy Steel
Properties	Weldability

E460 E Chemical Element Composition Content (%)

Component	C	Si	Mn ^②	P	S	Cr	Ni	Cu ^④	Mo	Ti ^③	V ^③	Nb ^③	Al ^③
Minimum Value	-	-	1	-	-	-	-	-	-	0.02	0.02	0.015	0.02
Maximum Value	0.2	0.5	1.7	0.025	0.025	0.7	1	0.7	0.4	0.2	0.2	0.06	-

① As the chemical composition influences the welding characteristics, if the purchaser so requests, the manufacturer shall, at the time of the order being placed, indicate the type of steel which he will supply and the maximum values or the range of the alloying elements which will be used in that steel.
② For products of thickness 6 mm or under, the manganese content may be reduced by 0.2 % (m/m).
③ The steels shall contain, in the percentage indicated in the Table, at least one of the grain-refining elements. If these elements are used in combination, the content for at least one of them shall be not less than the specified minimum value.
④ By agreement at the time of ordering, the maximum copper content may be 0.30 %(m/m).
⑤ Ceq=C+Mn/6+(Cr+Mo+V)/5+(Ni+Cu)/15

E460 E Mechanical Properties

thickness t mm	Tensile Strength σ_b Mpa	Specified Plastic Yield Strength Rp_0.2 Mpa	Elongation or Extension Rate δ %	Impact Energy Absorption KV2 J
t≤16	① 550~720	≥460	≥17	-50°C: long.: ≥27 tr.: ≥16 ②③
16＜t≤35	① 550~720	≥450	≥17	-50°C: long.: ≥27 tr.: ≥16 ②③
35＜t≤50	① 550~720	≥440	≥17	-50°C: long.: ≥27 tr.: ≥16 ②③
50＜t≤70	① 550~720	≥420	≥17	-50°C: long.: ≥27 tr.: ≥16 ②③
70＜t≤100	① 530~700	≥400	≥17	-50°C: long.: ≥27 tr.: ≥16 ②③
100＜t≤125	① 520~690	≥390	≥17	-50°C: long.: ≥27 tr.: ≥16 ②③
125＜t≤150	① 510~680	≥380	≥17	-50°C: long.: ≥27 tr.: ≥16 ②③

E460E Corresponding Standards(Same grade name, different standards)

1	ISO 4950-2-1995
	E460E
2	ISO 4950-3-1995
	E 460 E
3	JIS G 3128-1999(R2004)
	E460 E

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!