S30100 - ASTM A 666/A666M-2024

USA UNS	S30100
AISI American Iron and Steel Institute	301
Corresponding Standard	ASTM A666/A666M-2024 Standard Specification for Annealed or Cold-Worked Austenitic Stainless Steel Sheet, Strip, Plate, and Flat Bar
Classification	Austenitic Stainless Steel
Properties	Corrosion Resistance

Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Ni	N
Minimum Value	-	-	-	-	-	16	6	-
Maximum Value	0.15	1	2	0.045	0.03	18	8	0.1

Mechanical Properties

Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Hardness HBW
Annealing	≥515	≥205	≥40	≤217
1/16 Hard	≥620	≥310	≥40
1/8 Hard	≥690	≥380	≥40
1/4 Hard	≥860	≥515	≥25
1/2 Hard	≥1035	≥760	≥15 (thickness＜0.38mm); ≥18 (thickness≥0.38mm)
3/4 Hard	≥1205	≥930	≥10 (thickness＜0.38mm); ≥12 (thickness≥0.38mm)
Full Hard	≥1275	≥965	≥8 (thickness＜0.38mm); ≥9 (thickness≥0.38mm)
Super Full Hard	≥1860	≥1790	/

1 Approximate Comparison Table Austenitic Stainless Steel

China

Taiwan, China

Japan

South Korea

United States

International Organization for Standardization

Germany

France

European Standard

United Kingdom

ISC

CNS

JIS

ASTM

UNS

ISO

Numerical Grade

DIN EN/DIN

W-Nr.

NF EN/NF

Numerical Grade

BS EN/BS

12Cr17Ni7
(1Cr17Ni7)

S30110

301

SUS 301

STS 301

301

S30100

X5CrNi 17-7
X12CrNi17-7
14
(ISO 683-13:1986)

4319-301-00-I
4310-301-09-X

X10CrNi 18-8

1.4310

Z12CN 17-07
Z12CN 18-07

1.4319

301S21

2 Approximate Comparison Table Stainless Steels for Cold Heading and Cold Extruding

China		United States		International Organization for Standardization		European Standard
GB	ISC	ASTM/AISI	UNS	ISO	Numerical Grade	EN	Numerical Grade
12Cr17Ni7 (1Cr17Ni7)	S30110	301	S30100	X10CrNi18-8	4310-301-00-I	X10CrNi18-8	1.4310

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!