简体 | 繁體
Grade X3CrNiMo17-13-3
European Standard Steel Grade 1.4436
Corresponding Standard EN 10272-2016
Stainless steel bars for pressure purposes
Classification Austenitic Stainless Steel
X3CrNiMo17-13-3 Chemical Element Composition Content (%)
Component C Si Mn P S ① Cr Ni Mo N
Minimum Value - - - - - 16.5 10.5 2.5 -
Maximum Value 0.05 1 2 0.045 0.015 18.5 13 3 0.1
① Particular ranges of sulfur content may provide improvement of particular properties. For machinability, a controlled sulfur content of 0,015 % to 0,030 % is recommended and may be agreed. For weldability, a controlled sulfur content of 0,008 % to 0,030 % is recommended and may be agreed.
X3CrNiMo17-13-3 Mechanical Properties
Diameter or thickness
d or b
mm		 Tensile Strength
σb
Mpa 		Specified Plastic Yield Strength
Rp0.2
Mpa 		Elongation or Extension Rate
δ
% 		Hardness
HBW 		Impact Energy Absorption
KV2
J
≤160 500~700 Rp0.2：≥200
Rp1.0：≥235		 l: ≥40 ≤215 (at 20℃)：l ≥100
(at -196℃)：≥60
160<d (b)≤400 500~700 Rp0.2：≥200
Rp1.0：≥235		 tr: ≥30 ≤215 (at 20℃)：tr ≥60
(at -196℃)：≥ 60
a) Axial： l；Tangential：tr.
* The maximum HBW-values may be raised by 100 units or the tensile strength value may be raised by 200 MPa and the minimum elongation value be lowered to 20 % for bars of ≤ 35 mm thickness having a final cold deformation.
1 Approximate Comparison Table Austenitic Stainless Steel
China Taiwan, China Japan South Korea United States International Organization for Standardization Germany France European Standard Sweden United Kingdom
GB ISC CNS JIS KS ASTM UNS ISO Numerical Grade DIN EN/DIN W-Nr. NF EN/NF EN Numerical Grade SS BS EN/BS
06Cr17Ni12Mo2 S31608 316 SUS 316 STS 316 316 S31600 X5CrNiMo 17-12-2 4401-316-00-I X5CrNiMo 17-12-2
(X5CrNiMo 18-10)
X5CrNiMo 17-13-3
(X5CrNiMo 18-12) 		1.4401
1.4401
1.4436
1.4436 		Z6CND 17-11
Z6CND 17-12 		X5CrNiMo 17-12-2
X3CrNiMo 17-13-3 		1.4401
1.4436 		2347
2343 		316S16
316S31
2 Approximate Comparison Table Austenitic Heat-Resistant Steel
China Taiwan, China Japan South Korea United States International Organization for Standardization Germany France European Standard Russia Sweden United Kingdom
GB ISC CNS JIS KS ASTM UNS ISO DIN EN/DIN W-Nr. NF EN/NF EN Numerical Grade GOST SS BS EN/BS
06Cr17Ni12Mo2
(0Cr17Ni12Mo2)
0Cr18Ni12Mo2Ti 		S31608 316 SUS 316 STS 316 316 S31600 X5CrNiMo 17-12-2 X5CrNiMo 17-12-2
(X5CrNiMo 18-10)
X5CrNiMo 17-13-3
(X5CrNiMo 18-12) 		1.4401
1.4401
1.4436
1.4436 		Z6CND 17-11
Z6CND 17-12 		X5CrNiMo 17-12-2
X3CrNiMo 17-13-3 		1.4401
1.4436 		08Х17Н13М2Т 2347
2343 		316S16
316S31
3 Approximate Comparison Table Austenitic Stainless Steel
China United States European Standard
GB ISC ASTM/AISI UNS EN Numerical Grade
07Cr17Ni12Mo2
(1Cr17Ni12Mo2) 		S31609 316H S31609 X3CrNiMo 17-13-3 1.4436
4 Approximate Comparison Table Austenitic Stainless Steel
China Japan United States International Organization for Standardization France European Standard Sweden United Kingdom
GB JIS ASTM ISO NF EN/NF EN Numerical Grade SS BS EN/BS
0Cr17Ni12Mo2 SUS316 316 Type20a Z7CND18-12-03
Z7CND18-12-3 		X3CrNiMo17-13-3 1.4436 2343 316S31
316S33
X3CrNiMo17-13-3 Corresponding Standards(Same grade name, different standards)
1 EN 10088-1-2005
X3CrNiMo 17-13-3 1.4436
2 EN 10296-2-2005
X3CrNiMo17-13-3 1.4436
3 EN 10253-4-2003
X3CrNiMo 17-13-3 1.4436
4 EN 10263-5-2001
X3CrNiMo 17-13-3 1.4436
5 EN 10250-4-1999
X3CrNiMo 17-13-3 1.4436
6 EN 10088-2-2005
X3CrNiMo17-13-3 1.4436
7 EN 10088-3-2005
X3CrNiMo 17-13-3 1.4436
8 EN 10297(2)-2005
X3CrNiMo17-13-3 1.4436
9 EN 10088-3-2014
X3CrNiMo17-13-3 1.4436
10 DIN EN 10263-5-2018
X3CrNiMo 17-13-3 1.4436
11 DIN EN 10088-3-2014
X3CrNiMo17-13-3 1.4436
12 ISO 4954-2018
X3CrNiMo17-13-3 4436-316-00-I
13 NF EN 10088-2-2005
X3CrNiMo17-13-3 1.4436
14 NF EN 10088-1-2005
X3CrNiMo17-13-3 1.4436
15 NF EN 10028-7-2008
X3CrNiMo17-13-3 1.4436
16 NF EN 10296-2-2005
X3CrNiMo17-13-3 1.4436
17 NF EN 10028-7-2000
X3CrNiMo17-13-3 1.4436
18 EN 10263-5-2017
X3CrNiMo 17-13-3 1.4436
19 ISO 4954-2-2024
X3CrNiMo17-13-3 4436-316-00-I
20 DIN EN 10296-2-2006
X3CrNiMo17-13-3 1.4436
21 EN 10272-2016
X3CrNiMo17-13-3 1.4436

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!