X1NiCrMoCu25-20-5 1.4539 - EN 10272-2016

Grade	X1NiCrMoCu25-20-5
European Standard Steel Grade	1.4539
Corresponding Standard	EN 10272-2016 Stainless steel bars for pressure purposes
Classification	Austenitic Stainless Steel

X1NiCrMoCu25-20-5 Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Ni	Cu	Mo	N
Minimum Value	-	-	-	-	-	19	24	1.2	4	-
Maximum Value	0.02	0.7	2	0.03	0.01	21	26	2	5	0.15

X1NiCrMoCu25-20-5 Mechanical Properties

Diameter or thickness d or b mm	Tensile Strength σ_b Mpa	Specified Plastic Yield Strength Rp_0.2 Mpa	Elongation or Extension Rate δ %	Hardness HBW	Impact Energy Absorption KV2 J
≤160	530~730	Rp0.2：≥230 Rp1.0：≥260	l: ≥35	≤230	(at 20℃)：l ≥100 (at -196℃)：≥60
160<d (b)≤400	530~730	Rp0.2：≥230 Rp1.0：≥260	tr: ≥30	≤230	(at 20℃)：tr ≥60 (at -196℃)：≥ 60

a) Axial： l；Tangential：tr.

* The maximum HBW-values may be raised by 100 units or the tensile strength value may be raised by 200 MPa and the minimum elongation value be lowered to 20 % for bars of ≤ 35 mm thickness having a final cold deformation.

Approximate Comparison Table Austenitic Stainless Steel

China		Japan	United States		International Organization for Standardization		France	European Standard		Sweden	United Kingdom
GB	ISC	JIS	ASTM/AISI	UNS	ISO	Numerical Grade	NF EN/NF	EN	Numerical Grade	SS	BS EN/BS
015Cr21Ni26Mo5Cu2	S31782	SUS 890L	904L	N08904	X1NiCrMoCu25-20-5	4539-089-04-I	Z2NCDU25-20	X1NiCrMoCu25-20-5	1.4539	2562	904S13

X1NiCrMoCu25-20-5 Corresponding Standards(Same grade name, different standards)

1	EN 10088-1-2005
	X1NiCrMoCu 25-20-5 1.4539
2	EN 10296-2-2005
	X1NiCrMoCu25-20-5 1.4539
3	EN 10253-4-2003
	X1NiCrMoCu25-20-5 1.4539
4	EN 10250-4-1999
	X1NiCrMoCu 25-20-5 1.4539
5	ISO TS 15510-2003
	X1NiCrMoCu25-20-5
6	EN 10088-2-2005
	X1NiCrMoCu25-20-5 1.4539
7	EN 10088-3-2005
	X1NiCrMoCu 25-20-5 1.4539
8	EN 10088-3-2014
	X1NiCrMoCu25-20-5 1.4539
9	ISO 15510-2014
	X1NiCrMoCu25-20-5 4539-089-04-I
10	ISO 9328-7-2018
	X1NiCrMoCu25-20-5
11	DIN EN 10088-3-2014
	X1NiCrMoCu25-20-5 1.4539
12	DIN EN 10270-3-2012
	X1NiCrMoCu25- 20-5 1.4539
13	ISO 683-18-2014
	X1NiCrMoCu25-20-5 4539-089-04-I
14	NF EN 10088-2-2005
	X1NiCrMoCu25-20-5 1.4539
15	NF EN 10088-1-2005
	X1NiCrMoCu25-20-5 1.4539
16	NF EN 10028-7-2008
	X1NiCrMoCu25-20-5 1.4539
17	NF EN 10296-2-2005
	X1NiCrMoCu25-20-5 1.4539
18	NF EN 10028-7-2000
	X1NiCrMoCu25-20-5 1.4539
19	DIN EN 10296-2-2006
	X1NiCrMoCu25-20-5 1.4539
20	EN 10272-2016
	X1NiCrMoCu25-20-5 1.4539

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!