Home Material EN 10272-2016
简体 | 繁體
Grade X6CrNiNb18-10
European Standard Steel Grade 1.4550
Corresponding Standard EN 10272-2016
Stainless Steel Bars for Pressure Purposes
Classification Austenitic Stainless Steel
X6CrNiNb18-10 Chemical Element Composition Content (%)
Component C Si Mn P S Cr Ni More
Minimum Value - - - - - 17 9 Nb：10 x C ~ 1.00
Maximum Value 0.08 1 2 0.045 0.015 19 12
X6CrNiNb18-10 Mechanical Properties
Diameter or thickness
d or b
mm		 Tensile Strength
σb
Mpa 		Specified Plastic Yield Strength
Rp0.2
Mpa 		Elongation or Extension Rate
δ
% 		Hardness
HBW 		Impact Energy Absorption
KV2
J
≤160 510~740 Rp0.2：≥205
Rp1.0：≥240		 l: ≥40 ≤230 (at 20℃)：l ≥100
(at -196℃)：≥40
160<d (b)≤400 510~740 Rp0.2：≥205
Rp1.0：≥240		 tr: ≥30 ≤230 (at 20℃)：tr ≥60
(at -196℃)：≥ 40
a) Axial： l；Tangential：tr.
* The maximum HBW-values may be raised by 100 units or the tensile strength value may be raised by 200 MPa and the minimum elongation value be lowered to 20 % for bars of ≤ 35 mm thickness having a final cold deformation.
1 Approximate Comparison Table Austenitic Stainless Steel
China Taiwan, China Japan South Korea United States International Organization for Standardization Germany France European Standard Russia Sweden United Kingdom
GB ISC CNS JIS KS ASTM/AISI UNS ISO DIN EN/DIN W-Nr. NF EN/NF EN Numerical Grade GOST SS BS EN/BS
06Cr18Ni11Nb S34778 347 SUS 347 STS 347 347 S34700 X6CrNiNb 18-10 X6CrNiNb 18-10
(X10CrNiNb18-9) 		1.4550 Z6CNNb 18-10 X6CrNiNb 18-10 1.4550 08Х18Н12Б 2338 347S17
347S31
2 Approximate Comparison Table Austenitic Heat-Resistant Steel
China Taiwan, China Japan South Korea United States International Organization for Standardization Germany France European Standard Russia Sweden United Kingdom
GB ISC CNS JIS KS ASTM/AISI UNS ISO DIN EN/DIN W-Nr. NF EN/NF EN Numerical Grade GOST SS BS EN/BS
06Cr18Ni11Nb
(0Cr18Ni11Nb) 		S34778 347 SUS 347 STS 347 347 S34700 X6CrNiNb 18-10 X6CrNiNb 18-10
(X10CrNiNb18-9) 		1.4550 Z6CNNb 18-10 X6CrNiNb 18-10 1.4550 08Х18Н12Б 2338 347S17
347S31
3 Approximate Comparison Table Austenitic Stainless Steel
China International Organization for Standardization European Standard
GB ISO EN
0Cr18Ni10Nb X6CrNiNb18-10 X6CrNiNb18-10
X6CrNiNb18-10 Corresponding Standards(Same grade name, different standards)
1 EN 10088-1-2005
X6CrNiNb 18-10 1.4550
2 EN 10296-2-2005
X6CrNiNb18-10 1.4550
3 EN 10253-4-2003
X6CrNiNb18-10 1.4550
4 EN 10250-4-1999
X6CrNiNb 18-10 1.4550
5 ISO TS 15510-2003
X6CrNiNb18-10
6 EN 10088-2-2005
X6CrNiNb18-10 1.4550
7 DIN 17440-1972
X6CrNiNb 18-10 X10CrNiNb 18-9 1.4550
8 EN 10088-3-2005
X6CrNiNb 18-10 1.4550
9 ISO 9327(-5)-1999
X6CrNiNb18-10 (F50)
10 EN 10088-3-2014
X6CrNiNb 18-10 1.4550
11 ISO 15510-2014
X6CrNiNb18-10 4550-347-00-I
12 ISO 9328-7-2018
X6CrNiNb18-10
13 DIN EN 10088-3-2014
X6CrNiNb 18-10 1.4550
14 NF EN 10088-2-2005
X6CrNiNb18-10 1.4550
15 NF EN 10088-1-2005
X6CrNiNb18-10 1.4550
16 NF EN 10028-7-2008
X6CrNiNb18-10 1.4550
17 NF EN 10296-2-2005
X6CrNiNb18-10 1.4550
18 NF EN 10028-7-2000
X6CrNiNb18-10 1.4550
19 DIN EN 10296-2-2006
X6CrNiNb18-10 1.4550
20 EN 10272-2016
X6CrNiNb18-10 1.4550

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!