X2CrMnNiMoN21-5-3 1.4482 - EN 10272-2016

Grade	X2CrMnNiMoN21-5-3
European Standard Steel Grade	1.4482
Corresponding Standard	EN 10272-2016 Stainless steel bars for pressure purposes
Classification	Duplex Stainless Steel

X2CrMnNiMoN21-5-3 Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Ni	Cu	Mo	N
Minimum Value	-	-	4	-	-	19.5	1.5	-	0.1	0.05
Maximum Value	0.03	1	6	0.035	0.03	21.5	3.5	1	0.6	0.2

① Elements not quoted in this table shall not be intentionally added to the steel without the agreement of the purchaser except for finishing the cast. All appropriate precautions shall be taken to avoid the addition of such elements from scrap and other materials used in production which would impair mechanical properties and the suitability of the steel.

X2CrMnNiMoN21-5-3 Mechanical Properties

Diameter or thickness d or b mm	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Specified Plastic Yield Strength Rp_0.2 Mpa	Elongation or Extension Rate δ %	Hardness HBW	Impact Energy Absorption KV2 J
≤160	固溶	650~900	≥400	l: ≥25	≤290	(at 20℃)：l ≥100 (at -40℃)：l ≥60

a) Axial： l；Tangential：tr.

① The solution treatment may be omitted if the conditions for hot working and subsequent cooling are such that the requirements for the mechanical properties of the product and the resistance to intergranular corrosion as defined in EN ISO 3651-2 are obtained.
② The tensile strength value may be raised by 200 MPa and the minimum elongation value be lowered to 20 % for bars having a final cold defonnation.

Approximate Comparison Table Austenitic-Ferritic Stainless Steel

International Organization for Standardization		European Standard
ISO	Numerical Grade	Numerical Grade
X2CrMnNiMoN21-5-3	4482-320-01-X	1.4482

X2CrMnNiMoN21-5-3 Corresponding Standards(Same grade name, different standards)

1	ISO 15510-2014
	X2CrMnNiMoN21-5-3 4482-320-01-X
2	EN 10272-2016
	X2CrMnNiMoN21-5-3 1.4482

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!