Grade QSt36-3
Germany W-Nr. 1.0214
Corresponding Standard DIN 1654-2-1989
Cold Heading and Extruding Steels Technical Delivery Conditions for Killed Unalloyed Steels Not Intended for Heat Treatment
Classification Carbon Steel
Properties Forgability
QSt36-3 Chemical Element Composition Content (%)
Component C Si Mn P S Al
Minimum Value 0.06 - 0.25 - - 0.02
Maximum Value 0.13 0.1 0.45 0.04 0.04 -
QSt36-3 Mechanical Properties
condition Heat Treatment or Condition
Tensile Strength
σb
Mpa 		Yield Point
σs
Mpa 		Elongation or Extension Rate
δ
% 		Reduction of Area
ψ
% 		Impact Energy Absorption
KV2
J
Hot-rolled bar stock Untreated and Descaled (U+SH) ≤430 - - ≥60 -
Normalizing 320~430 ≥200 ≥30 - ≥27
New and Old Grade Replacement List
Corresponding Standard Grade
DIN 1654-2-1989
Grade
Germany W-Nr.
DIN EN 10263-2-2017
Grade
Germany W-Nr.
1 Approximate Comparison Table Cold Heading Steel
China Taiwan, China Japan South Korea United States International Organization for Standardization Germany France Russia United Kingdom
GB ISC CNS JIS KS ASTM/AISI UNS ISO DIN EN/DIN W-Nr. NF EN/NF GOST BS EN/BS
ML10 U40102 SWRCH10K SWRCH10K SWRCH10K 1012 G10120 CC8A
(A2Al) 		QSt36-3
(C11C) 		1.0214 XC10
FB10
FR10 		10кл 0/2
2 Approximate Comparison Table High-Quality Carbon Structural Steel
Germany European Standard
DIN EN/DIN EN Numerical Grade
QSt36-3 C10C 1.0214
3 Approximate Comparison Table Steel for Cold Heading and Cold Extrusion
China Japan South Korea United States International Organization for Standardization Germany United Kingdom
GB JIS KS ASTM ISO DIN EN/DIN BS EN/BS
ML10Al SWRCH10A SWCH10A 1012 CC8A QSt36-3 0/2