S355J0H 1.0547 - EN 10219-1-2006

Grade	S355J0H
European Standard Steel Grade	1.0547
Corresponding Standard	EN 10219-1-2006 Cold Formed Welded Structural Hollow Sections of Non-Alloy and Fine Grain Steels - Part 1: Technical Delivery Conditions
Classification	Carbon Steel

S355J0H Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	N ^②	More
Minimum Value	-	-	-	-	-	-	CEV: ≤ 0.45%
Maximum Value	0.22	0.55	1.6	0.035	0.035	0.009	CEV: ≤ 0.45%

① The deoxidation method Is designated as follows: FF Fully killed steel containing nitrogen binding elements in amounts sufficient to bind available nitrogen (e.g. min. 0,020 % total Al or 0,015 % soluble Al).
② The maximum value for nitrogen does not apply if the chemical composition shows a minimum total Al content of 0,020 % with a minimum Al/N ratio of 2:1, or if sufficient other N-binding elements are present. The N-binding elements shall be recorded in the Inspection Document.

S355J0H Mechanical Properties

Thickness t mm	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Impact Energy Absorption KV2 J
t≤16		ReH: ≥355	① ≥20
16＜t≤40		ReH: ≥345	≥20
t≤3	510~680
3＜t≤40	470~630
				≥27

S355J0H Corresponding Standards(Same grade name, different standards)

1	EN 10210-1-2006
	S355J0H 1.0547
2	EN 10219-1-2006
	S355J0H 1.0547

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!