ML10Al U40108 - GB /T 28906-2025

Grade	ML10Al
China ISC	U40108
Corresponding Standard	GB /T 28906-2025 Hot Rolled Wire Rod for Cold Heading
Classification	Carbon Steel
Properties	Good Forgability

ML10Al Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Al ^①
Minimum Value	0.08	-	0.3	-	-	0.02
Maximum Value	0.13	0.1	0.6	0.025	0.02	0.06

ML10Al Mechanical Properties

diameter d mm	Tensile Strength σ_b Mpa	Reduction of Area ψ %
d≤12	≤430	≥60
d＞12	≤430	≥55

1 Approximate Comparison Table Steel for Cold Heading and Cold Extrusion

China		Japan	United States	International Organization for Standardization	European Standard
GB	ISC	JIS	ASTM	ISO	EN	Numerical Grade
ML10Al	U40108	SWRCH10A	1010	C10C	C10C	1.0214

2 Approximate Comparison Table Steel for Cold Heading and Cold Extrusion

China	Japan	South Korea	United States	International Organization for Standardization	Germany	United Kingdom
GB	JIS	KS	ASTM	ISO	DIN EN/DIN	BS EN/BS
ML10Al	SWRCH10A	SWCH10A	1012	CC8A	QSt36-3	0/2

3 Approximate Comparison Table Steel for Cold Heading and Cold Extrusion

China		Japan	United States	International Organization for Standardization	European Standard
YB	GB	JIS	ASTM	ISO	EN
QML10Al	ML10Al	SWRCH10A	1010	C10C	C10C

4 Approximate Comparison Table Steel for Cold Heading and Cold Extrusion

China	Japan	International Organization for Standardization	European Standard
GB	JIS	ISO	EN	Numerical Grade
ML10Al	SWRCH10A	C10C	C10C	1.0214

5 Approximate Comparison Table Steel for Cold Heading and Cold Extrusion

China		Japan	United States	International Organization for Standardization	European Standard
GB	ISC	JIS	ASTM	ISO	EN
ML10Al	U40108	SWRCH10A	1010	CC11A	C10C

ML10Al Corresponding Standards(Same grade name, different standards)

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!