00Ni18Co12Mo5TiAl C350 18Ni-350 - GJB 10310-2021

Grade	00Ni18Co12Mo5TiAl
Other Names
Corresponding Standard	GJB 10310-2021 Specification for Ultra-high Strength Maraging Steel Forgings
Classification	Special Alloy Steel

00Ni18Co12Mo5TiAl Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Ni	Cu	Mo	Ti	Co	Al
Minimum Value	-	-	-	-	-	-	17.5	-	4	1.25	11.5	0.05
Maximum Value	0.008	0.1	0.1	0.005	0.005	0.5	19	0.5	5.2	1.6	12.5	0.15

The addition of calcium (Ca) may be permitted, provided that the total content does not exceed 0.05%.

00Ni18Co12Mo5TiAl Mechanical Properties

Sampling direction	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Specified Plastic Yield Strength Rp_0.2 Mpa	Elongation or Extension Rate δ %	Reduction of Area ψ %	Hardness HBW
Longitudinal	Solution treatment: 820°C ± 10°C, 1 hour, air cooling to room temperature; Aging treatment: 510°C ± 10°C, 1 to 4 hours, air cooling to room temperature.	≥2255	≥2155	≥5	≥38	HRC：≥52 ①

① When tensile properties meet the requirements, hardness may not be used as an acceptance criterion; only measured values shall be provided.

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!