Home Material EN 10217-7-2021
简体 | 繁體
Grade X2CrNiMoN 22-5-3
European Standard Steel Grade 1.4462
Corresponding Standard EN 10217-7-2021
Part 7: Stainless steel tubes
Classification Duplex Stainless Steel
X2CrNiMoN 22-5-3 Chemical Element Composition Content (%)
Component C Si Mn P * S * Cr Ni Mo N
Minimum Value - - - - - 21 4.5 2.5 0.1
Maximum Value 0.03 1 2 0.035 0.015 23 6.5 3.5 0.22
* For tubes welded without filler material the sum of sulphur and phosphorus shall be maximum 0,040 %.
X2CrNiMoN 22-5-3 Mechanical Properties
wall thickness
T
mm		 Heat Treatment or Condition
Tensile Strength
σb
Mpa 		Specified Plastic Yield Strength
Rp0.2
Mpa 		Elongation or Extension Rate
δ
% 		Impact Energy Absorption
KV2
J
T≤60 Solution annealing (+AT) 700~920 ≥450 ≥25(l)
≥20(t)		 室温
≥120(l)；≥90(t)
-40°C
≥40(t)
• l=longitudinal；t=transverse
• Solution annealing temperature: 1020-1100°C, rapid cooling in water and air. Resistant to intergranular corrosion. Method B or C in EN ISO 3651-2-1998.
1 Approximate Comparison Table Austenitic-Ferritic Stainless Steel
China Taiwan, China Japan South Korea United States International Organization for Standardization Germany France European Standard
GB ISC CNS JIS KS UNS ISO Numerical Grade DIN EN/DIN W-Nr. NF EN/NF EN Numerical Grade
022Cr22Ni5Mo3N
022Cr23Ni5Mo3N 		S22253
S22053 		329J3L SUS 329J3L STS 329J3L S31803
S32205 		X2CrNiMoN 22-5-3 4462-318-03-I X2CrNiMoN 22-5-3 1.4462 X2CrNiMoN 22-5-3 X2CrNiMoN 22-5-3 1.4462
2 Approximate Comparison Table Austenitic-Ferritic Stainless Steel
United States France European Standard Sweden United Kingdom
UNS NF EN/NF EN Numerical Grade SS BS EN/BS
S32205 Z3CND22-05Az X2CrNiMoN22-5-3 1.4462 2377 318S13
3 Approximate Comparison Table Stainless Steels for Cold Heading and Cold Extruding
China Japan United States International Organization for Standardization European Standard
GB ISC JIS ASTM/AISI UNS ISO Numerical Grade EN Numerical Grade
022Cr23Ni5Mo3N S22053 SUS329J3L 2205 S32205 X2CrNiMoN22-5-3 4462-318-03-I X2CrNiMoN22-5-3 1.4462
X2CrNiMoN22-5-3 Corresponding Standards(Same grade name, different standards)
1 EN 10088-1-2005
X2CrNiMoN 22-5-3 1.4462
2 EN 10296-2-2005
X2CrNiMoN22-5-3 1.4462
3 EN 10253-4-2003
X2CrNiMoN22-5-3 1.4462
4 EN 10263-5-2001
X2CrNiMoN22-5-3 1.4462
5 EN 10250-4-1999
X2CrNiMoN 22-5-3 1.4462
6 ISO TS 15510-2003
X2CrNiMoN22-5-3
7 EN 10088-3-2005
X2CrNiMoN22-5-3 1.4462
8 EN 10297(2)-2005
X2CrNiMoN22-5-3 1.4462
9 ISO 9327(-5)-1999
X2CrNiMoN22-5-3
10 EN 10088-3-2014
X2CrNiMoN22-5-3 1.4462
11 ISO 15510-2014
X2CrNiMoN22-5-3 4462-318-03-I
12 DIN EN 10263-5-2018
X2CrNiMoN22-5-3 1.4462
13 ISO 9328-7-2018
X2CrNiMoN22-5-3
14 DIN EN 10088-3-2014
X2CrNiMoN22-5-3 1.4462
15 DIN EN 10270-3-2012
X2CrNiMoN22-5-3 1.4462
16 ISO 683-18-2014
X2CrNiMoN22-5-3 4462-318-03-I
17 ISO 4954-2018
X2CrNiMoN22-5-3 4462-318-03-I
18 NF EN 10088-2-2005
X2CrNiMoN22-5-3 1.4462
19 NF EN 10088-1-2005
X2CrNiMoN22-5-3 1.4462
20 NF EN 10028-7-2008
X2CrNiMoN22-5-3 1.4462
21 NF EN 10296-2-2005
X2CrNiMoN22-5-3 1.4462
22 NF EN 10028-7-2000
X2CrNiMoN22-5-3 1.4462
23 EN 10263-5-2017
X2CrNiMoN22-5-3 1.4462
24 ISO 4954-2-2024
X2CrNiMoN22-5-3 4462-318-03-I
25 DIN EN 10296-2-2006
X2CrNiMoN22-5-3 1.4462
26 EN 10272-2016
X2CrNiMoN22-5-3 1.4462
27 EN 10217-7-2021
X2CrNiMoN 22-5-3 1.4462
28 EN 10088-2-2024
X2CrNiMoN22-5-3 1.4462
29 EN 10028-7-2016
X2CrNiMoN22-5-3 1.4462

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!