Grade X6CrNiTi18-10
Old Grade
Corresponding Standard ISO 9327(-5)-1999
Steel Forgings and Rolled or Forged Bars for Pressure Purposes-Technical Delivery Conditions-Part 5:Stainless Steels
Classification Austenitic Stainless Steel
Properties Corrosion Resistance
X6CrNiTi18-10 Chemical Element Composition Content (%)
Component C Si Mn P S Cr Ni More
Minimum Value - - - - - 17 9 Ti：5×C~0.8
Maximum Value 0.08 1 2 0.045 0.03 19 12
X6CrNiTi18-10 Mechanical Properties
thickness
t
mm		 Tensile Strength
σb
Mpa 		Yield Point
σs
Mpa 		Elongation or Extension Rate
δ
%
t≤450 510~710 ≥200 ≥30
1 Approximate Comparison Table Austenitic Stainless Steel
China Taiwan, China Japan South Korea United States International Organization for Standardization Germany France European Standard Russia Sweden United Kingdom
GB ISC CNS JIS KS ASTM UNS ISO Numerical Grade DIN EN/DIN W-Nr. NF EN/NF EN Numerical Grade GOST SS BS EN/BS
06Cr18Ni11Ti S32168 321 SUS 321 STS 321 321 S32100 X6CrNiTi 18-10 4541-321-00-I X6CrNiTi 18-10
(X10CrNiTi 18-9) 		1.4541 Z6CNT 18-10 X6CrNiTi 18-10 1.4541 09Х18Н10Т
Х18Н10Т 		2337 321S12
321S31
2 Approximate Comparison Table Austenitic Heat-Resistant Steel
China Taiwan, China Japan South Korea United States International Organization for Standardization Germany France European Standard Russia Sweden United Kingdom
GB ISC CNS JIS KS ASTM UNS ISO DIN EN/DIN W-Nr. NF EN/NF EN Numerical Grade GOST SS BS EN/BS
06Cr18Ni11Ti
(0Cr18Ni11Ti) 		S32168 321 SUS 321 STS 321 321 S32100 X6CrNiTi 18-10 X6CrNiTi 18-10
(X10CrNiTi 18-9) 		1.4541 Z6CNT 18-10 X6CrNiTi 18-10 1.4541 09Х18Н10Т 2337 321S12
321S31
3 Approximate Comparison Table Stainless Steels for Cold Heading and Cold Extruding
China Japan United States International Organization for Standardization European Standard
GB ISC JIS ASTM/AISI UNS ISO Numerical Grade EN Numerical Grade
06Cr18Ni11Ti
(0Cr18Ni11Ti) 		S32168 SUS321 321 S32100 X6CrNiTi18-10 4541-321-00-I X6CrNiTi18-10 1.4541
X6CrNiTi18-10 Corresponding Standards(Same grade name, different standards)
1 EN 10088-1-2005
X6CrNiTi 18-10 1.4541
2 EN 10296-2-2005
X6CrNiTi18-10 1.4541
3 EN 10253-4-2003
X6CrNiTi18-10 1.4541
4 EN 10263-5-2001
X6CrNiTi18-10 1.4541
5 EN 10250-4-1999
X6CrNiTi 18-10 1.4541
6 ISO TS 15510-2003
X6CrNiTi18-10
7 EN 10088-2-2005
X6CrNiTi18-10 1.4541
8 EN 10088-3-2005
X6CrNiTi 18-10 1.4541
9 EN 10297-2-2005
X6CrNiTi18-10 1.4541
10 ISO 9327(-5)-1999
X6CrNiTi18-10 (F53)
11 EN 10088-3-2014
X6CrNiTi 18-10 1.4541
12 ISO 15510-2014
X6CrNiTi18-10 4541-321-00-I
13 DIN EN 10263-5-2018
X6CrNiTi18-10 1.4541
14 ISO 9328-7-2018
X6CrNiTi18-10
15 DIN EN 10088-3-2014
X6CrNiTi 18-10 1.4541
16 ISO 683-18-2014
X6CrNiTi18-10 4541-321-00-I
17 ISO 4954-2018
X6CrNiTi18-10 4541-321-00-I
18 NF EN 10088-2-2005
X6CrNiTi18-10 1.4541
19 NF EN 10088-1-2005
X6CrNiTi18-10 1.4541
20 NF EN 10028-7-2008
X6CrNiTi18-10 1.4541
21 NF EN 10296-2-2005
X6CrNiTi18-10 1.4541
22 NF EN 10028-7-2000
X6CrNiTi18-10 1.4541
23 EN 10263-5-2017
X6CrNiTi18-10 1.4541
24 ISO 4954-2-2024
X6CrNiTi18-10 4541-321-00-I
25 DIN EN 10296-2-2006
X6CrNiTi18-10 1.4541
26 EN 10272-2016
X6CrNiTi18-10 1.4541
27 EN 10217-7-2021
X6CrNiTi 18-10 1.4541
28 EN 10088-2-2024
X6CrNiTi18-10 1.4541
29 EN 10028-7-2016
X6CrNiTi18-10 1.4541
30 DIN EN 10263-5-2002
X6CrNiTi18-10 1.4541

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!