302 SAE 30320 - SAE AMS 5636F-2012

Grade	302
Other Names
Corresponding Standard	SAE AMS 5636F-2012 Steel, Corrosion-Resistant, Bars and Wire 18Cr - 9.0Ni(SAE 30302) Solution Heat Treated and Cold Drawn 100ksi(689Mpa) Tensile Strength
Classification	Austenitic Stainless Steel
Properties	Corrosion Resistance Forgability Machinability Weldability
Density	7.92 g/cm³

302 Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Ni	Cu	Mo
Minimum Value	-	-	-	-	-	17	8	-	-
Maximum Value	0.15	1	2	0.04	0.03	19	10	0.75	0.75

302 Mechanical Properties

codnition	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Reduction of Area ψ %
Bar, Wire rod; d≤19	Solution treatment, cold drawing, heating to 371±14°C, descaling	≥689	≥414	≥32	≥50

Approximate Comparison Table Austenitic Stainless Steel

China

Taiwan, China

Japan

South Korea

United States

International Organization for Standardization

Germany

France

European Standard

Russia

United Kingdom

ISC

CNS

JIS

ASTM

UNS

ISO

Numerical Grade

DIN EN/DIN

W-Nr.

NF EN/NF

Numerical Grade

GOST

BS EN/BS

12Cr18Ni9
(1Cr18Ni9)

S30210

302

SUS 302

STS 302

302

S30200

X10CrNi 18-8
12
(ISO 683-13:1986)

4310-301-00-I

X12CrNi 18-8

1.4300

Z10CN 18-09

X10CrNi 18-8

1.4310

12Х18Н9

302S25

302 Corresponding Standards(Same grade name, different standards)

1	ASTM A959-2004
	302 S30200
2	ASTM A240/240M-2018
	302 S30200
3	SAE J405-1998
	302 S30200
4	ASTM A493-2009(2013)
	302 S30200
5	SAE J467b-1956(R1968)
	302
6	ASTM A276/A276M-2017
	302 S30200
7	SAE AMS 5636F-2012
	302 SAE 30320
8	SAE AMS 5516R-2019
	302 18Cr - 9.0Ni
9	GB 2100-1980
	302 ZG0Cr18Ni9
10	ASTM A473-2018
	302 S30200
11	SAE J405-2018
	302 S30200
12	ASTM A313/A313M-2018
	302 S30200
13	ASTM F899-2020
	302 S30200
14	ASTM A493-2016
	302 S30200
15	ASTM A240/A240M-2020
	302 S30200
16	ASTM A959-2019
	302 S30200
17	SAE AMS5688L-2007(R2012)
	302 SAE 30302
18	ASTM A479/A479M-2018
	302 S30200
19	CNS 3477-2016
	302
20	ASTM A666/A666M-2024
	302 S30200

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!