0Cr18Ni12Mo2Ti - GB /T 1220-1992

Grade	0Cr18Ni12Mo2Ti
Corresponding Standard	GB /T 1220-1992 Stainless steel bars
Classification	Austenitic Stainless Steel
Properties	Corrosion Resistance

0Cr18Ni12Mo2Ti Chemical Element Composition Content (%)

Component	C	Si	Mn	P	S	Cr	Ni	Mo	More
Minimum Value	-	-	-	-	-	16	11	1.8	Ti：5×C~0.7
Maximum Value	0.08	1	2	0.035	0.03	19	14	2.5	Ti：5×C~0.7

0Cr18Ni12Mo2Ti Mechanical Properties

diameter d mm	Heat Treatment or Condition	Tensile Strength σ_b Mpa	Yield Point σ_s Mpa	Elongation or Extension Rate δ %	Reduction of Area ψ %	Hardness HBW
d=25	Solution heat treatment 1000~1100°C rapid cooling	≥530	≥205	≥40	≥55	≤187

1 Approximate Comparison Table Austenitic Heat-Resistant Steel

China

Taiwan, China

Japan

South Korea

United States

International Organization for Standardization

Germany

France

European Standard

Russia

Sweden

United Kingdom

ISC

CNS

JIS

ASTM

UNS

ISO

DIN EN/DIN

W-Nr.

NF EN/NF

Numerical Grade

GOST

BS EN/BS

06Cr17Ni12Mo2
(0Cr17Ni12Mo2)
0Cr18Ni12Mo2Ti

S31608

316

SUS 316

STS 316

316

S31600

X5CrNiMo 17-12-2

X5CrNiMo 17-12-2
(X5CrNiMo 18-10)
X5CrNiMo 17-13-3
(X5CrNiMo 18-12)

1.4401
1.4401
1.4436
1.4436

Z6CND 17-11
Z6CND 17-12

X5CrNiMo 17-12-2
X3CrNiMo 17-13-3

1.4401
1.4436

08Х17Н13М2Т

2347
2343

316S16
316S31

2 Approximate Comparison Table Austenitic Stainless Steel

China	Japan	United States	International Organization for Standardization	Germany	France	European Standard		Sweden	United Kingdom
GB	JIS	ASTM	ISO	DIN EN/DIN	NF EN/NF	EN	Numerical Grade	SS	BS EN/BS
00Cr17Ni14Mo2 0Cr18Ni12Mo2Ti	SUS316 SUS316L	316L	Type19	X2CrNiMo17-13-2	Z2CND17-12 Z3CND17-11-02 Z3CND18-12-02	X2CrNiMo17-12-2	1.4404	2348	316S11

3 Approximate Comparison Table Austenitic Stainless Steel

China	Japan	United States	Germany	France	European Standard		Russia	Sweden	United Kingdom
GB	JIS	ASTM	DIN EN/DIN	NF EN/NF	EN	Numerical Grade	GOST	SS	BS EN/BS
0Cr18Ni12Mo2Ti 1Cr18Ni12Mo2Ti	316Ti SUS316Ti	316Ti	X10CrNiMoTi18-10 X6CrNiMoTi17-12-2	Z6CNDT17-12 Z6CNT17-12	X6CrNiMoTi17-12-2	1.4571	08KH17N13M2T 10KH17N13M2T	2350 2350-02	320S31 321S12

4 Approximate Comparison Table Austenitic Stainless Steel

China	Germany	France	Russia	United Kingdom
GB	DIN EN/DIN	NF EN/NF	GOST	BS EN/BS
0Cr18Ni12Mo2Ti	X10CrNiMoTi1810	Z6CNDT17.12	08X17H13M2T	320S17

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!