N08811 alloy 800HT - ASTM B 408-2022

USA UNS	N08811
Other Names
Corresponding Standard	ASTM B 408-2022 Standard Specification for Nickel-Iron-Chromium Alloy Rod and Bar
Classification	Alloy Steel

Chemical Element Composition Content (%)

Component	Fe ^①	C	Si	Mn	P	S	Cr	Ni	Cu	Ti	Al	More
Minimum Value	39.5	0.06	-	-	-	-	19	30	-	0.25	0.25	Al+Ti=0.85-1.20
Maximum Value	-	0.1	1	1.5	0.045	0.015	23	35	0.75	0.6	0.6	Al+Ti=0.85-1.20

① Iron shall be determined arithmetically by difference.

Mechanical Properties

Heat Treatment or Condition	Tensile Strength σ_b Mpa	Specified Plastic Yield Strength Rp_0.2 Mpa	Elongation or Extension Rate δ %
Cold-worked and hot-worked, annealed	≥450	≥170	≥30

1 Approximate Comparison Table Corrosion-Resistant Alloy

2 Approximate Comparison Table Austenitic Stainless Steel

United States	International Organization for Standardization		European Standard
UNS	ISO	Numerical Grade	Numerical Grade
N08811	X8NiCrAlTi33-21	4959-088-11-U	1.4959

3 Approximate Comparison Table Corrosion-Resistant Alloy

Note: The data is for reference only! If you have any questions, please fill out "I want to correct it"!